Anodic alumina membranes as template for the synthesis of 1-D metal oxide and hydroxide nanostructures
2008
Anodic alumina membranes with highly ordered cylindrical pores and tuneable geometry have been prepared (pore diameters=20−200 nm; pore density 1012-1014 pores/m2; thickness: 20-100 mm) by controlling the anodizing process of aluminum in phosphoric, oxalic and sulphuric acid. The influence of different parameters (initial treatment of aluminium surface, composition of electrolyte, temperature and applied potential) on the final characteristics of the membranes have been investigated. The use anodic alumina membranes as template for the electrosynthesis of some metal hydroxides and oxides 1-D nanostructures (nanowires and nanotubes) will be also proved.
Optical and magnetic properties of ZnCoO thin films synthesized by electrodeposition
2008
Ternary Zn1−xCoxO crystalline films with different compositions were grown by electrodeposition. The Co content in the final compound is linked to the initial Co/Zn ratio in the starting solution. X-ray diffraction reveals a wurtzite structure for the Zn1−xCoxO films. Transmittance spectra show two effects proportional to Co content, a redshift of the absorption edge and three absorption bands, which are both interpreted to be due to the Co incorporated into the ZnO lattice. The amount of deposited charge was used to get a precise control of the film thickness. Magnetic measurements point out that Co(II) ions are isolated from each other, and consequently the films are paramagnetic. Francis…
High-performance of PbO2 nanowire electrodes for lead-acid battery
2014
Abstract PbO2 nanowires were obtained by template electrodeposition in polycarbonate membranes and tested as positive electrode for lead-acid battery. Nanowires were grown on the same material acting as current collector that was electrodeposited too. The nanostructured electrodes were assembled in a zero-gap configuration using commercial negative plate and separator. Cell performance was tested by galvanostatic charge/discharge cycles in a 5 M H2SO4 aqueous electrolyte. PbO2 nanostructured electrodes were able to deliver at 1C rate an almost constant capacity of about 190 mAh g−1 (85% of active material utilization), close to the theoretical value (224 mAh g−1). The nanowire array provide…
Fabrication and Characterisation of Perovskite Thin Films for Photovoltaic Application
2018
This paper presents an alternative way to obtain perovskite thin films for photovoltaic application. This technique results more competitive, scalable, low-cost, reproducible and is different from other most common methods of fabrication.
Dual Ni/Ni-Co electrodeposited coatings for improved erosion-corrosion behaviour
2019
Abstract Industrial applications of hydrophobic metallic coatings are limited to durability of their surface structures against detrimental effects of the surrounding environments. In the present research, the life-long of the hierarchical structure of hydrophobic nickel coating in an erosive-corrosive solution was investigated. The effect of alloying with cobalt on strengthening the hierarchical structures was also investigated. In this regard, highly hydrophobic Ni/Ni, Ni-Co/Ni-Co, dual Ni/Ni-Co and dual Ni-Co/Ni coatings with rough hierarchical structures were electrodeposited. In situ electrochemical measurements were performed to investigate changes in corrosion resistance and hydropho…
Parametrical study of multilayer structures for CIGS solar cells
2014
In this paper, a numerical analysis of relevant electrical parameters of multilayer structures for CIGS-based solar cells was carried out, employing the simulation software wxAMPS. In particular, we have focused on thin film cells having a ZnO:Al/ZnO/CdS/CIGS structure with a Molybdenum back contact. The aim of this work is to establish good theoretical reference values for an ongoing experimental activity, where our technology of choice is the single-step electrodeposition. In detail, we have analyzed how the main electrical properties change with the bang gap and the thickness of the absorber layer, for such a type of solar cell structure. Our results show that both efficiency and fill fa…
Double Step Electrochemical Process for the Deposition of Superhydrophobic Coatings for Enhanced Corrosion Resistance
2021
Superhydrophobic surface on anodized AA5083 sample was obtained by an electrochemical process. Scanning Electron Microscopy and Fourier Transform Infrared Spectroscopy analyses revealed the hierarchical structure of the coating and the presence of manganese stearate. These features were crucial for the coating superhydrophobicity, demonstrated by a measured contact angle of ~ 163° and its self-cleaning ability. Electrochemical characterization in an aqueous solution mimicking seawater proved an enhanced corrosion resistance due to the superhydrophobic coating with respect to anodized AA5083 sample that also lasted after 20 immersion days in Cl- containing electrolyte.
Electrodeposition of supported gadolinium-doped ceria solid solution nanowires
2012
Gadolinium-ceria solid solution nanowires with tunable composition have been prepared through template cathodic electrodeposition from solutions containing Ce 3+Gd 3+ in a variable ratio. The employed template is Porous Anodic Alumina because it can function as thermal resistant separator supporting the nanowires if used as ionic conductor in Solid Oxide Fuel Cell (SOFC). Scanning Electron Microscopy of the deposited nanostructures revealed that the use of ethanol as solvent and metal chloride as electrolyte allowed to prepare continuous, compact and well defined nanowires with morphological features stable even after thermal treatment. EDX compositional analysis confirms the presence of bo…
Room temperature electrodeposition of photoactive Cd(OH)2 nanowires
2009
Cd(OH)2 nanowires (NWs) were successfully prepared by room temperature electrogeneration of base using Cd(NO3)2 aqueous electrolyte and Anodic Alumina Membrane (AAM) as template. Cd(OH)2 films have been also deposited on tin-doped indium oxide (ITO) for comparison. SEM analysis shows high quality deposits made of closely packed nanowires (NWs) into AAM and uniform flake-like surface on ITO. XRD analysis reveals that Cd(OH)2 films on ITO are polycrystalline, while the nanowires grow along the preferential directions [100] and [110]. Photoelectrochemical measurements show that Cd(OH)2 NWs are photoactive materials with indirect and direct band gap of 2.15 and 2.75 eV, respectively. Keywords: …
Anodic Electro Deposition of CeO2 and Co-Doped CeO2 Thin Films
2013
CeO2 and Co containing CeO2 thin films were deposited on indium tin oxide and stainless steel by anodic electrodeposition. Scanning electron microscopy showed that the films are flat and show globular morphology and cracks resulting from volume shrinking. According to XRD and Raman Spectroscopy pure ceria layers are crystalline, while the presence of Co induces the formation of amorphous films. The good adhesion and the compactness allowed the photoelectrochemical characterization of the films. A band gap value of 2.9 eV was estimated for CeO2, while slightly higher values (̃3.0 eV) were estimated for Co containing films. A mechanism for ceria anodic electrodeposition is proposed and discus…