Thermoanalytical study of nucleating effects in polypropylene composites
1996
Interfacial structure plays an important role in the performance of polypropylene composites. Transcrystalline interfacial layer were determined in talc filled polypropylene. The crystallization and melting behaviour of talc and CaCC3 filled polypropylene could be modified with smaller amount of additives like elastomer and surfactants. Through the effect of these additives the structure of interface and the degree of crystallinity could be controlled in filled polypropylene.
Structure and Mechanical Properties of Melt Intercalated Po1lypropylene–Organomontmorillonite Nanocomposites
2010
The preparation and properties of polymer nanocomposites, obtained by melt-compounding of polypropylene (PP) and organomontmorillonite (OMMT) modified by different alkyl ammonium salts, are described. A copolymer of maleic anhydride and PP was used as a compatibilizing additive. Nanocomposites with OMMT content of 1, 5 and 10 wt% were prepared and tested. The influence of OMMT content on the tensile stress–strain curves, elastic modulus, yield and tensile strength, and ultimate elongation of the nanocomposites is determined. The results of measuring the microhardness and impact strength of polymer nanocomposites are presented. Long-term creep tests were performed to predict the long-term de…
Synthesis and characterization of redox-sensitive polyurethanes based on L-glutathione oxidized and poly(ether ester) triblock copolymers
2021
Abstract Segmented polyurethanes, based on PCL-PEG-PCL copolymers, 1,4-diisocyanatobutane and l -glutathione oxidized, used as chain extender, were synthetized. Three different reactions conditions were investigated using three different copolymers having ɛ-CL/polyethylene glycol molar ratios equal to 12, 24 and 36 and three different reaction conditions. As investigated by size exclusion chromatography analyses and quantification of l -glutathione, the polymerization and the extension phase's efficiency depended on the ɛ-CL/PEG ratio and the extension phase's operating temperature. Three selected polyurethanes were characterized by spectroscopic, differential scanning calorimetry (DSC) and…
Preparation, Characterization and Photocatalytic Activity of TiO2 Impregnated with the Heteropolyacid H3PW12O40: Photo-assisted Degradation of 2-prop…
2009
Abstract Both commercial and home prepared TiO2 samples impregnated with tungstophosphoric acid (H3PW12O40) were prepared and used for the photo-assisted degradation of 2-propanol in gas–solid regime. The characterization results evidenced a good coverage of the polyoxometalate (POM) onto the surface of both types of TiO2 samples along with a marginal effect of the presence of ethanol or HCl during the POM impregnation step on the specific surface area, porosity, morphology, crystallinity and acidity of the samples. Propene was the main intermediate product found in 2-propanol photocatalytic degradation by using the samples containing POM as the photocatalyst, whereas propanone was mainly o…
Numerical Simulations on the Growth of Thin Oxide Films on Aluminum Substrates
2010
We investigated the oxidation of nanocrystalline aluminum surfaces by using variable charge molecular dynamics at 600 K under three oxygen pressures: 1, 10 and 20 atm. The interaction potential was described by the electrostatic plus (Es+) model that allows dynamical charge transfer among atoms. We mainly focused on the effect of the oxygen pressure on the oxidation kinetic, the chemical composition and the microstructure of the oxide films formed. The results show that oxidation kinetics as well as chemical composition and microstructure depend on the applied oxygen pressure. The oxide film thickness tends to a limiting value equal to ~3 nm. Finally, we obtained a partially crystalline oxi…
Doped ZnS:Mn nanoparticles obtained by sonochemical synthesis.
2010
A study of sonochemically synthesized ZnS:Mn nanoparticles is presented. The particles prepared at low rf power (about 20 W) and room temperature coalesce to form morphologically amorphous large species (30-100 nm in diameter). As the power is increased in the range from 20 to 70 W, and the solution temperature is raised to 60 to 80 degrees C, finer particles are produced with the size ranging from 2 to 20 nm and improved crystallinity. The results indicate the dispersion of the Mn(2+) ions at near-surface sites in the particles. It is shown that the sonochemically fabricated particles approach the quality of the ones obtained by a standard chemical route and show a reasonable luminescence …
Synthesis, characterization and foaming of PHEA-PLLA, a new graft copolymer for biomedical engineering
2014
Abstract In this study a chemical grafting procedure was set up in order to link high molecular weight poly L-lactic acid (PLLA) chains to the hydrophilic α,β-poly(N-2-hydroxyethyl)-DL-aspartamide (PHEA) backbone. A graft copolymer named PHEA-g-PLLA (or simply PHEA–PLLA) was obtained bearing a degree of derivatization of 1.0 mol.% of PLLA as grafted chain. This new hybrid derivative offers both the opportune crystallinity necessary for the production of scaffolds trough a thermally induced phase separation (TIPS) technique and the proper chemical reactivity to perform further functionalizations with bio-effectors and drugs. PHEA–PLLA porous scaffolds for tissue engineering applications were…
XRMA analysis and X-ray diffraction analysis of dental enamel from human permanent teeth exposed to hydrogen peroxide of varying pH
2019
Background This in vitroinvestigation shows how 3.3% H2O2, at different pH-values affects the enamel. Material and Methods A number of fifteen human premolars were used. The enamel of the coronal half in six of the teeth, were exposed by H2O2. Nine teeth were prepared to enamel powder. The enamel was exposed to 3.3% H2O2, at six different pH-values (pH range 4.5 - 7.0). Analyses of the topography of enamel performed by scanning electron microscope (SEM) and the chemical composition of enamel by X-ray microanalysis (XRMA). X-ray powder diffraction (XRD) analysed the crystallinity in enamel powder. Results The exposure to H2O2 at pH5.5 resulted in a decrease of O in the exposed enamel, and ch…
Poly lactic acid based foams prepared via thermally induced phase separation (TIPS): A method to tune the crystallinity
2012
Blends of Poly-L-Lactic Acid (PLLA) with two Poly-Lactic Acid (PLA) in different proportions (90/10 and 70/30) were utilized in order to produce biodegradable and biocompatible scaffolds for soft tissue engineering applications. The scaffolds were produced via thermally induced phase separation (TIPS) starting from ternary systems where dioxane was the solvent and water the non-solvent. Morphology was evaluated by Scanning Electron Microscopy (average pore size and interconnection). Moreover a DSC analysis was carried out on the as-obtained scaffold in order to obtain information about theirs thermal properties (enthalpy of melt and crystallization). The results showed that is possible to p…
Development and Characterization of Silver-Based Antimicrobial Ethylene–Vinyl Alcohol Copolymer (EVOH) Films for Food-Packaging Applications
2012
The use of silver as an antimicrobial in the food area has raised wide interest in recent years. In the present work, 0.001-10 wt % silver ions was satisfactorily incorporated into an ethylene-vinyl alcohol (EVOH) copolymer matrix by a solvent casting technique. The antibacterial efficacy of the composite was evaluated under laboratory conditions and in contact with some foods. The ionic compound did not affect the crystallinity or the water-induced plasticization of the materials and was homogeneously distributed across the surface and thickness of the films. When immersed in water, sorption-induced release of 50-100% of the silver ions took place in30 min. In the bacterial minimal growth …