Mixed mode energy release rates for bonded composite joints
2011
Abstract: Analytical formulae developed by Luo and Tong (2009) to determine the mixed mode strain energy release rates of laminated and co-cured composite structures and joints are reviewed. The effects of varying loading conditions and geometries on the mode mixity found analytically are investigated via a parametric study. A critical evaluation of the analytical formulae indicates that the formulae are robust in calculating the total strain energy release rate, but may underestimate the mode II component compared with the finite element analysis and experimental results. Possible reasons for this discrepancy are discussed, including the effect of stress concentrations and singularities at…
Competition between the buckling-driven delamination and wrinkling in compressed thin coatings
2012
Abstract The competition between two common failure modes of a thin coating under in-plane compression, the surface wrinkling and the buckling-driven delamination, is studied to assess the critical strain when the mechanical instability may occur at given geometrical and material parameters. A buckling map is constructed based on results of a finite element analysis, which relates the critical applied strain for the onset of instability to the interface adhesion and elastic properties of materials. An approximate scaling relation is derived for the energy release rate of buckling-driven delamination of a coating deposited on a compliant substrate.
Crack growth analysis at adhesive–adherent interface in bonded joints under mixed mode I/II
2008
The propagation of an interface crack subjected to mixed mode I/II was investigated for two 2024-T351 aluminum thin layers joined by means of DP760 epoxy adhesive produced by 3M©. On the basis of beam theory, an analytical expression for computing the energy release rate is presented for the mixed-mode end loaded split (MMELS) test. The analytical strain energy release rate was compared by finite element (FE) analysis using the virtual crack closure technique (VCCT). Several fatigue crack growth tests were carried out in a plane bending machine to compare the experimental energy release rates to those of the analytical and FE solutions. Experimental results showed the relationship between t…
Debonding failure mechanisms in prestressed CFRP/epoxy/concrete connections
2014
Abstract This paper presents an investigation on the failure mode in prestress force-release tests of CFRP strips bonded to concrete substrates. Background of the study is the gradient anchorage technique. Firstly, experimental test series are presented. It is shown that considerable differences in failure mechanisms between lap-shear and the before mentioned release tests exist. The study reveals a strong Mode I-influence in the debonding process, compared to a Mode II for lap-shear tests. Secondly, FE simulations with a commercially available software are introduced. It is demonstrated that delamination in a force-release test occurs by a mixed-mode failure over the strip width.
Non associative damage interface model for mixed mode delamination and frictional contact
2019
Abstract The present paper proposes a new interface constitutive model based on the non-associative damage mechanics and frictional plasticity. The model is developed in a thermodynamically consistent framework, with three independent damage variables. The non associative flow rules drive the concurrent evolution of the three damage variables. The interface model provides two independent values for the mode I fracture energy and the mode II fracture energy and it is able to accurately reproduce arbitrary mixed mode fracture conditions. The model can also take into account the presence of frictional effects both at the fully debonded zones and at the partially debonded ones. The experimental…
Analytical Solution of the 4ENF Test with Interlaminar Frictional Effects and Evaluation of Mode II Delamination Toughness
2018
The present paper proposes an analytical solution of the four points bend end-notched flexure test (4ENF) with frictional contact between the delamination surfaces. The analytical solution was developed in the framework of the classic Euler-Bernoulli bending beam theory with orthotropic linear elastic constitutive behavior. The frictional contact was modeled as rigid-perfectly plastic with the Mohr-Coulomb activation function and the nonassociative flow rule. The elastic solution of the partially cracked beam subjected to the four points bending test with frictional contact was developed, and the Mode II delamination toughness was analytically determined by means of the Griffith approach, a…
Interlaminar fracture toughness behavior of electron-beam cured carbon-fiber reinforced epoxy-resin composites
2013
The work describes the preparation and physical-mechanical characterization of unidirectional CFRP panels manufactured by an electron beam curing technique. Delamination fracture toughness in Mode I and II is investigated in order to evaluate the influence of fiber–matrix adhesion strength, matrix toughness and matrix crosslinking density as determined by the radiation curing process. A matrix system comprising a DGEBA epoxy monomer and an initiator of cationic polymerization have been used, with one batch of resin mixed with a PES monomer in order to enhance matrix toughness. Curing was achieved with a pulsed 10 MeV Electron Beam accelerator. Thermally cured composite systems have also bee…
Estimation of interfacial fracture toughness based on progressive edge delamination of a thin transparent coating on a polymer substrate
2010
Evaluation of interfacial toughness of sub-micron-thickness layers deposited on a ductile substrate is a challenging task which has motivated different experimental approaches Fragmentation testing was used in the present study as a means of interface characterization of a silicon-nitride-coated polyimide substrate. During the test, after an initial rapid segmentation-cracking phase, the coating fragments developed edge delaminations which propagated in a stable manner with further increase in the applied strain The debonding process was modelled by the finite element method Incorporating a cohesive zone at the front of the interfacial crack The edge cracks were found to be dominated by mod…
Effects of fiber orientation of adjacent plies on the mode I crack propagation in a carbon-epoxy laminates
2011
Abstract The influence of ply orientation on the resistance to mode I delamination of multidirectional composite laminates can be assessed by Double Cantilever Beam (DCB) tests. However, one of the difficulties associated with such a study is the change in overall elastic parameters occurring when modifying local ply orientations. The present work uses laminates with special stacking sequences allowing for isolating the orientation parameter. Multidirectional DCB specimens were designed so as to obtain an uncoupled quasi isotropic and quasi-homogeneous elastic behavior, with the same properties for the entire laminate and the two sub laminates separated by the pre crack at mid-plane. The re…
Micromechanisms of load transfer in a unidirectional carbon fibre-reinforced epoxy composite due to fibre failures: Part 3. Multiscale reconstruction…
2008
International audience; This third article describes a multiscale process which takes into account the most important microscopic phenomena associated with composite degradation, including fibre fractures and interfacial debonding, overloading of fibres neighbouring a fibre break as well as viscoelastic behaviour of the matrix. The results have been used to accurately predict the macroscopic failure of unidirectional carbon fibre-reinforced epoxy and quantify damage accumulation in pressure vessels made of the same material. The approach described has allowed the acoustic emission activity resulting from fibres breaks to be evaluated and shown how the residual lifetimes of such vessels, whe…