Influence of sodium bicarbonate treatment on the aging resistance of natural fiber reinforced polymer composites under marine environment
2019
Abstract Aim of the current study is to investigate how an innovative and eco-friendly chemical treatment based on sodium bicarbonate solution (10 wt%) can improve the aging resistance in marine environment of epoxy based composites, reinforced with flax and jute fibers. To this scope, treated and untreated fiber reinforced composites were manufactured through vacuum infusion technique. The resulting composites were then exposed to salt-fog spray conditions up to 60 days, according to ASTM B117 standard. The assessment of their durability was made by means of tensile, flexural quasi-static tests and Charpy impact tests. Furthermore, the water uptake evolution of each composite was monitored…
Pinned hybrid glass-flax composite laminates aged in salt-fog environment: Mechanical durability
2019
The aim of the present paper is to study the mechanical performance evolution of pinned hybrid glass-flax composite laminates under environment aging conditions. Hybrid glass-flax fibers/epoxy pinned laminates were exposed to salt-spray fog environmental conditions up to 60 days. With the purpose of assessing the relationship between mechanical performances and failure mechanisms at increasing aging time, single lap joints at varying joint geometry (i.e., hole diameter D and hole distance E from free edge) were characterized after 0 days (i.e., unaged samples), 30 days, and 60 days of salt-fog exposition. Based on this approach, the property&ndash
New concept in bioderived composites: Biochar as toughening agent for improving performances and durability of agave-based epoxy biocomposites
2021
Biocomposites are increasingly used in the industry for the replacement of synthetic materials, thanks to their good mechanical properties, being lightweight, and having low cost. Unfortunately, in several potential fields of structural application their static strength and fatigue life are not high enough. For this reason, several chemical treatments on the fibers have been proposed in literature, although still without fully satisfactory results. To overcome this drawback, in this study we present a procedure based on the addition of a carbonaceous filler to a green epoxy matrix reinforced by Agave sisalana fibers. Among all carbon-based materials, biochar was selected for its environment…
Experimental assessment of the improved properties during aging of flax/glass hybrid composite laminates for marine applications
2018
The investigation for natural fibers composites in terms of performance, durability, and environmental impact for structural applications in marine environments is a relevant challenge in scientific and industrial field. On this context, the aim of this work is to assess the durability and mechanical stability in severe environment of epoxy/glass–flax hybrid composites. For the sake of comparison, also full flax and glass epoxy composites were investigated. All samples were exposed to salt–fog environmental conditions up to 60 aging days. Wettability behavior during time was compared with water uptake evolution to assess water sensitivity of hybrid composite configurations. Moreover, quasi-…
Effect of glass fiber hybridization on the durability in salt-fog environment of pinned flax composites
2021
The aim of the present paper is to evaluate the effect of the hybridization with external layers of glass fibers on the durability of flax fiber reinforced composites in severe aging conditions. To this scope, full glass, full flax and hybrid glass–flax pinned laminates were exposed to a salt-fog environment for up to 60 days. Double-lap pinned joint tests were performed to assess the pin-hole joints performances at varying the laminate stacking sequence. In order to better discriminate the relationship between the mechanical behavior and the fracture mechanisms of joints at increasing the aging time, different geometries (i.e., by varying both the hole diameter D and the free edge distance…
Photochemical stabilization of linear low-density polyethylene/clay nanocomposites: Towards durable nanocomposites
2008
International audience; This article reports a study of the chemical modifications of LLDPE/nanoblend nanocomposites exposed to UV light in conditions of artificially accelerated ageing and natural weathering. Analysis by infrared spectroscopy of the chemical modifications produced by photoageing shows that the presence of an organo-clay leads to the decrease of the oxidation induction time of the polymer (LLDPE), which results in lower durability of the nanocomposites. Protection against photooxidation was tested with different kinds of UV stabilizers and with a metal deactivator. It is shown that the metal deactivator is very efficient in stabilizing the nanocomposite since it totally can…
Degradation and Recycling of Films Based on Biodegradable Polymers: A Short Review
2019
The environmental performance of biodegradable materials has attracted attention from the academic and the industrial research over the recent years. Currently, degradation behavior and possible recyclability features, as well as actual recycling paths of such systems, are crucial to give them both durability and eco-sustainability. This paper presents a review of the degradation behaviour of biodegradable polymers and related composites, with particular concern for multi-layer films. The processing of biodegradable polymeric films and the manufacturing and properties of multilayer films based on biodegradable polymers will be discussed. The results and data collected show that: poly-lactic…
Degradation of polymer blends: A brief review
2017
Abstract The usefulness of any material, including polymer blends, depends on its degradability and durability. The blend composition can significantly affect the degradative behavior of a polymer blend and can differ from the degradation routes of the pure components since the interactions among different species in the blends during degradation, and among the degradation products, can occur. These reactions can lead either to an acceleration of the degradation rate or to a stabilizing effect in comparison with the pure components. Thus, the additive rule cannot be often applied in case of degradation of polymer blends and, therefore, it is difficult to predict the degradative behavior of …
Magnitude and distribution of stresses in composite resin and sound dentine interface with mechanical retentions
2014
Background: Adhesive systems are constantly subjected to mechanical and chemical stresses that negatively impact the integrity and durability of the dentine-adhesive interface. Despite the lack of evidence to support or reject the clinical indication for mechanical retention, the potential further contribution of these preparations to the behavior of the composite resin-sound dentine bond has been rarely addressed. The authors evaluated by finite element analysis the effect of mechanical retention on the magnitude and distribution of stresses in a composite resin-sound dentin bonding interface when subjected to tensile and shear forces. Material and Methods: A three-dimensional model was cr…
Rutting analysis of different rubberised stone mastic asphalt mixtures: from binders to mixtures
2021
Stone Mastic Asphalt (SMA) has been broadly used on heavily trafficked roads and motorways in the UK due to its known stability and durability. In this study, several sets of SMA mixtures were produced using different rubberised bitumens, including a Fischer–Tropsch wax pre-treated rubberised bitumen. Properties associated with rutting were evaluated using both linear and nonlinear viscoelastic analyses, using different test methods such as the Strategic Highway Research Programme (SHRP), Shenoy rutting parameter, zero shear viscosity (ZSV) and multiple stress creep recovery (MSCR) tests. The rutting resistance of the resulting SMA mixtures was assessed using the Repeated Load Axial Test (R…