Impact of electron beam irradiation on fish gelatin film properties
2016
International audience; The objective of this work was to display the effect of electron beam accelerator doses on properties of plasticized fish gelatin film. Electron spin resonance indicates free radical formation during irradiation, which might induce intermolecular cross-linking. Tensile strength for gelatin film significantly increases after irradiation (improved by 30% for 60 kGy). The vapour permeability is weakly affected by irradiation. Surface tension and its polar component increase significantly and are in accordance with the increase of wettability. So, irradiation may change the orientation of polar groups of gelatin at the film surface and crosslink the hydrophobic amino aci…
Effect of Oxidized Potato Starch on the Physicochemical Properties of Soy Protein Isolate-Based Edible Films
2013
The influence of oxidized starch on the physicochemical properties of cast soy protein isolate films is determined in this study. Films were cast from heated (70 °C for 20 min) alkaline (pH=10) aqueous solutions of 7 % soy protein isolate containing 50 % (by mass) glycerol as a plasticizer and different levels of added oxidized starch (0, 5, 10, 15, and 20 %, by mass). For all types of films, opacity, contact angle, tensile strength, elongation at break, water vapour permeability, measured at 25 °C for four relative humidity differentials (30–53, 30–75, 30–84 and 30–100 %), differential scanning calorimetry and microstructure were determined after conditioning film specimens at 25 °C and 30…
Effect of Oxidized Potato Starch on the Physicochemical Properties of Soy Protein Isolate-Based Edible Films
2013
The influence of oxidized starch on the physicochemical properties of cast soy protein isolate films is determined in this study. Films were cast from heated (70 °C for 20 min) alkaline (pH=10) aqueous solutions of 7 % soy protein isolate containing 50 % (by mass) glycerol as a plasticizer and different levels of added oxidized starch (0, 5, 10, 15, and 20 %, by mass). For all types of films, opacity, contact angle, tensile strength, elongation at break, water vapour permeability, measured at 25 °C for four relative humidity differentials (30–53, 30–75, 30–84 and 30–100 %), differential scanning calorimetry and microstructure were determined after conditioning film specimens at 25 °C and 30…
Effect of oil lamination between plasticized starch layers on film properties
2016
International audience; To reduce the hygroscopic character of biodegradable starch-based films, rapeseed oil was incorporated by lamination (starch-oil-starch 3-layers technique). The lipid lamination followed by starch solution casting step induced an emulsion type structure of dried films. Composite films are more opalescent and glossier than fatty free starch films. For all the films, structure is heterogeneous in the cross-section only. Adding fat induced a twice decrease of the tensile strength. Thermal gravimetry analysis did not show differences between films with and without oil. Lipid reduced the moisture absorption particularly at higher RH as well as the surface swelling index, …