Search results for "Electron microscope"
showing 10 items of 784 documents
Enhancement of self-sustaining reaction Cu3Si phase formation starting from mechanically activated powders
2000
Mechanical high-energy ball milling of an 3Cu Si elemental powders mixture was used to activate a self-sustaining combustion reaction or so-called self-sustaining high-temperature synthesis (SHS) to form the copper silicide phase, a reaction for which the thermodynamic criterion proposed by Munir for self-propagation reaction is not favorable. A complete characterization of the end-products was performed with X-ray diffraction analysis and scanning electron microscopy. Thermal and structural information describing the combustion front initiated by heating up a sample to 180°C in a Cu:Si system is communicated. This paper clearly shows that the mechanically activated self-sustaining high-tem…
Material transport and organizing phenomena of Langmuir—Blodgett membranes from polymerizable built up diacetylene amphiphiles on hydrophobic supports
1986
Abstract Langmuir—Blodgett multilayers of polymerized diin amphiphiles on different porous, hydrophobic ultrafilters have been studied as composite membranes under the conditions of reverse osmosis. Influences of differently structured surfaces of the supports on structure and phase change occurring during polymerization have been investigated by scanning electron microscopy and X-ray diffraction and are discussed with reverse osmosis data. When conditioned, fine porous hydrophobic supports become permeable to aqueous solutions at low pressures. Under these conditions permeate flux and retention were found to depend on the number of layers deposited.
Photocatalytic activity of non-stoichiometric ZnFe2O4under visible light irradiation
2014
Nanostructured zinc ferrites with different excess iron contents (ZnFe2+zO4, where z = 0.00, 0.05, 0.10 and 0.15) have been synthesized using the sol–gel auto-combustion method. The effect of excess iron on the structural, optical and visible light photocatalytic activity of zinc ferrite samples has been investigated. X-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), x-ray magnetic circular dichroism (XMCD), Brunauer–Emmett–Teller theory, scanning electron microscopy (SEM), diffuse reflectance spectroscopy (UV–Vis) and photoluminescence spectroscopy were used to characterize the synthesized non-stoichiometric ZnFe2O4 powders. The XRD patterns demonstrated that the samples con…
Photoactivity under visible light of metal loaded TiO2 catalysts prepared by low frequency ultrasound treatment
2017
Abstract Visible-light responsive bare and metal loaded (Pt, Ag, Rh, Pd) TiO 2 photocatalysts were prepared by using a simple ultrasound treatment. This method induced bulk oxygen deficiency resulting in a narrowing bandgap (from 3.18 to 3.04 eV) and in visible light absorption. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), BET specific surface area (SSA) and pore size distribution (PSD), UV–vis diffuse reflectance spectroscopy (DRS), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The photocatalytic activity of the samples was evaluated by using the 4-nitrophenol oxidation reaction and the photocatalytic oxidation of glucose w…
Influence of calcination on the structural properties of earth abundant Cu2ZnSnS4
2021
Abstract In the present work, we report on the synthesis of nano-crystalline kesterite copper zinc tin sulfide (CZTS) in powder form and the post-annealing process at high temperatures (calcination), and study their physical properties. We have successfully synthesized CZTS by direct fusion, and the resulting material was crushed to obtain a fine powder. Then, the resulting powder was calcined at high temperatures: 800–1000 ∘C. The calcined samples have been characterized with a number of different structural: X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and optical techniques: photoluminescence (PL), Raman and diffuse reflectance spectr…
Absolute crystallinity and photocatalytic activity of brookite TiO2 samples
2017
Abstract This study reports a method to determine the absolute crystallinity of partly crystalline brookite TiO2 photocatalysts. A natural, a commercial and various home-prepared brookite powders were characterized by X-ray diffraction analysis, Raman spectroscopy, scanning electron microscopy, UV–vis diffuse reflectance spectroscopy and nitrogen adsorption measurements. The absolute crystallinity was calculated from the ratio between the full width at half maximum intensity of the (121) X-ray diffraction peaks of the brookite samples and the (111) peak of CaF2 as internal standard. The photocatalytic activity of the powders was tested employing the photodegradation of 4-nitrophenol as well…
Photocatalytic degradation enhancement in pickering emulsions stabilized by solid particles of bare TiO 2
2019
Pickering emulsions provide a new way to enhance the efficiency of photocatalytic degradation of water-insoluble pollutants. Indeed, the semiconductor solid particles dually act as the photocatalyst and stabilizer of the emulsion droplets whose size dramatically affects the photocatalytic reaction. The present work aims at the validation of this concept by using bare TiO 2 without any surface modification. Nanostructured TiO 2 has been prepared by a simple sol-gel process and characterized by X-ray diffraction, specific surface area analysis, scanning electron microscopy, and diffuse reflectance spectroscopy. The emulsions were prepared by using 1-methylnaphthalene (1-MN) as a model organic…
Enhanced Solar Light Photocatalytic Activity of Ag Doped TiO2–Ag3PO4 Composites
2020
Composites comprised of Ag3PO4 and bare TiO2 (TiO2@Ag3PO4) or silver doped TiO2 (Ag@TiO2&ndash
Comparative study of air and vacuum annealing atmosphere towards Pt/Ti–W/SiO2 stability
2013
Abstract The thermal stability of Pt/Ti–W/SiO2 system was studied after annealing under air or vacuum in the present work. A Ti–W adhesive film (30 at. % Ti) was deposited on a SiO2 substrate followed by a thicker Pt layer. Depositions were performed using DC magnetron sputtering. The whole as-deposited films are metallic with a columnar growth of platinum deposit which totally wets the substrate. Whatever the atmosphere is, annealing at 500 °C for 12 h does not change the platinum state but modifies the morphology of platinum particles, the lateral average size of which increasing from less than 10 nm up to ca. 75 nm. Besides, a noticeable diffusion of metallic tungsten through Pt film is …
High temperature oxidation of higher manganese silicides
2021
Abstract The oxidation kinetics and mechanisms of higher manganese silicides (HMS) MnSi1.75, MnSi (1.75-x)Gex, MnSi(1.75-x)Alx (with x = 0.005 and 0.01)were studied and the effects of densification methods and dopant concentration discussed. Oxidation experiments were conducted using thermogravimetry (TGA), while post characterization with X-ray Photoelectron Spectroscopy (XPS) and Scanning Electron Microscope (SEM) showed that spark plasma sintering (SPS) is a better densification method than hot pressing (HP). Except for undoped HMS, HMS doped with 0.5at% Ge had the lowest oxidation rate. Stable formation of a SiO2 protective layer was the main reason for improved oxidation resistance in …