In vitro antibacterial activity of endodontic sealers
2004
Summary Objectives To evaluate the antibacterial activity of four endodontic sealers: one epoxy resin sealer (AH Plus), two zinc oxide eugenol (ZOE)-based sealers (Endomethasone, Pulp Canal Sealer), and one sealer containing both ZOE and orthophenilphenol (Vcanalare). Methods A direct contact test (DCT) was performed. A 10 μl suspension of Enterococcus faecalis was placed on the test material 20 min, 24 h and 7 days after mixing. Bacteria were allowed to directly contact the sealers for 1 h at 37 °C. Bacterial growth was then spectrophotometrically measured every 30 min for 7 h, and again after 24 h as well. Results All freshly mixed sealers showed complete inhibition of bacterial growth. S…
The adaptation of mechanically softened gutta-percha to the canal walls in the presence or absence of smear layer: a scanning electron microscopic st…
1995
Summary The objective of this study was to compare the adaptation of mechanically softened gutta-percha to the root canal wall in the presence and absence of smear layer. The root canals of 20 freshly extracted human maxillary incisors were cleaned and shaped. Prior to obturation, 10 root canals were irrigated with 20 ml of 50% citric acid followed by 20 ml of 5.25% sodium hypochlorite. All canals were obturated with mechanical compaction of gutta-percha and AH-26 sealer. After 72h, each tooth was fractured in half. Scanning electron microscopy demonstrated that the sealer had formed a continuous layer in contact with the canal walls, becoming progressively thinner towards the apex. The sea…
A free plate model can predict guided modes propagating in tubular bone-mimicking phantoms
2014
The goal of this work was to show that a non-absorbing free plate model can predict with a reasonable accuracy guided modes measured in bone-mimicking phantoms that have circular cross-section. Experiments were carried out on uncoated and coated phantoms using a clinical axial transmission setup. Adjustment of the plate model to the experimental data yielded estimates for the waveguide characteristics (thickness, bulk wave velocities). Fair agreement was achieved over a frequency range of 0.4 to 1.6 MHz. A lower accuracy observed for the thinnest bone-mimicking phantoms was caused by limitations in the wave number measurements rather than by the model itself.
Epoxy resins as a matrix material in advanced fiber-reinforced polymer (FRP) composites
2013
Abstract: This chapter discusses the epoxy resins which, thanks to their good and versatile properties, can be considered nowadays the most important class of thermosetting polymers. In particular the chapter first reviews both the epoxy resins commonly available on the market, including a new class of bio-derived epoxy resins, and the most-used curing agents. it then describes the principal characteristics of the epoxy resins and how it is possible to enhance them by adding several fillers to the epoxy system. Finally, the chapter analyzes the main engineering fields in which epoxy resins find application today and their possible future utilization.
Electrospun rubber/thermoplastic hybrid nanofibers for localized toughening effects in epoxy resins
2020
Synthetic rubber/thermoplastic blends were electrospun from their solutions. The rubber was a solid acrylonitrile/butadiene/acrylic acid copolymer and the thermoplastic was polyacrylonitrile. The aims of this study were to identify suitable systems and processing conditions for obtaining rubber-based electrospun nanofibers, to investigate the ability of an epoxy resin system to impregnate and swell selected hybrid rubber/thermoplastic mats, and to assess the impact of the nanofibers on the resin morphology and curing behavior. In particular, electrospinning trials were carried out varying the composition of the feed solution and process parameters, such as the applied voltage, the flow rate…
Carbon fibre composite materials produced by gamma radiation induced curing of epoxy resins
2008
It is well known that ionizing radiation can initiate polymerization of suitable monomers for many applications. In this work an epoxy dlfunctional monomer has been used as matrix of a carbon fibre composite in order to produce materials through gamma radiation, for aerospace and advanced automotive applications. Radiation curing has been performed at different absorbed doses and, as comparison, also thermal curing of the same monomer formulations has been done. Furthermore some Irradiated samples have been also subjected to a post Irradiation thermal curing in order to complete the polymerization reactions. The properties of the cured materials have been studied by moisture absorption isot…
High energy radiation cure of resin systems for structural adhesives and composite applications
2002
Abstract Radiation cure polymerisation of a commercial diglycidyl ether of bisphenol F epoxy resin has been achieved using a 60Co irradiation source, compounding the monomer with few percentage of an onium salt catalyst. The cure process has been monitored by a gamma-calorimetric technique and systems irradiated at doses corresponding to different positions in the gamma-calorimetric curve have been characterised via solubility tests and dynamic mechanical torsion analysis. Changes in both the measured gel fractions and tan δ values were associated with the progress of polymerisation and crosslinking reactions and these were dose dependent. Furthermore, systems irradiated at lower doses exhi…
E-beam curing of epoxy based blends in order to produce high performance composites
2007
In this work, blends of a difunctional epoxy monomer and a thermoplastic toughening agent are E-beam irradiated at two different dose rates and two different total absorbed doses. The influence of the processing conditions on the thermal properties and on the morphology of the obtained matrices has been investigated. In particular, it is shown how the increase of the dose rate causes an increase of the temperature during irradiation, thus inducing a simultaneous thermal and radiation curing. On the contrary, at low-dose rate the system mainly undergoes to radiation curing, thus making the cured material very sensible to a post-irradiation thermal treatment with a significant improvement of …
Accelerated ageing due to moisture absorption of thermally cured epoxy resin/polyethersulphone blends. Thermal, mechanical and morphological behaviour
2011
Abstract A model epoxy resin/anhydride system, modified with a polyethersulfone (PES) engineering thermoplastic toughening agent, has been studied under hydrothermal ageing in order to investigate the modification of the thermal, morphological and mechanical behaviour through dynamical mechanical thermal analysis, SEM microscopy and fracture toughness test respectively. Two different concentrations of the toughening agent were used in the blends and two ageing conditions have been considered, consisting of the immersion of the samples in distilled water at constant temperature of 70 °C for 1 week and for 1 month. Dynamical mechanical thermal analysis results on hydrothermally aged materials…
Thermal properties of e-beam cured epoxy/thermoplastic matrices for advanced composite materials
2007
The aim of this work is to investigate the possibility to improve the thermal behaviour of epoxy based systems, cured by ionizing radiation, in order to produce matrices for advanced carbon fibres composites. Blends of two epoxy monomers, difunctional and trifunctional, have been polymerized by e-beam irradiation and the dynamic mechanical thermal properties have been investigated. The increase of the concentration of the trifunctional epoxy monomer in the blend causes a marked increase of the Tg, but strongly decreases the reactivity. Subsequently, blends of the same epoxy monomers with a high Tg thermoplastic toughening agent have been considered and their reactivity and the thermal prope…