Total oxidation of propane using nanocrystalline cobalt oxide and supported cobalt oxide catalysts
2008
Abstract Supported and unsupported nanocrystalline cobalt oxides have been shown to be extremely efficient catalysts for the total oxidation of propane. Total conversion with a high stability has been achieved at reaction temperatures as low as 250 °C. In the present work, a comparison between the catalytic performance of bulk and alumina-supported nanocrystalline cobalt oxide catalysts has been made. The influence of crystallite size, nature of the support (alpha, gamma and mesoporous alumina) and cobalt loading, has been probed. Unsupported cobalt oxide catalysts were more active than any supported cobalt oxide catalysts. The catalytic activity was mainly dependent on the crystallite size…
Optimized bath for electroless deposition of palladium on amorphous alumina membranes
2006
A new bath for the electroless deposition of palladium on anodic alumina (AA) membranes is proposed. It was found that the optimal conditions for the uniform deposition of palladium, with minimal damage to the AA membranes, were under conditions of pH 8.4 and plating times shorter than 30 min. The deposited Pd layer was detected by X-ray diffraction (XRD) and energy dispersive X-ray (EDX) analysis. The morphology of the AA membrane before and after plating was examined by scanning electron microscopy (SEM). EDX analysis revealed that palladium was deposited only on the surfaces of the membrane and Sn ions, coming from the sensitizing bath, were incorporated into the palladium layer. EDTA in…
Covalently modified nanoclays: synthesis, properties and applications
2020
Abstract Clay minerals are phyllosilicates of nanoscale dimensions. According to their ability to entrap and release organic moieties, they have found applications in several fields, such as drug carrier and delivery, support for catalyst, environmental remediation and filler for polymeric matrices. The possibility to modify, by covalent linkage, their surfaces gives the possibility to form new nanomaterials with improved properties respect to the pristine clay minerals. In this chapter, the modifications of the siloxane surfaces of the most representative clay minerals, namely montmorillonite, sepiolites, laponite and halloysite were reviewed and discussed.
Microstructure Characteristics of Unsaturated Compacted Scaly Clay
2012
Microstructure characteristics of unsaturated compacted scaly clay are investigated by MIP tests on freeze dried samples and observation of SEM photomicrographs. Effects of scale microstructure and increasing compaction stresses, and microstructure changes induced by loading and unloading paths and clay saturation are analysed.
Calcium silicate hydrates: Solid and liquid phase composition
2015
© 2015 Elsevier Ltd. This paper presents a review on the relationship between the composition the structure and the solution in which calcium silicate hydrate (C S H) is equilibrated. The silica chain length in C S H increases with the silicon concentration and the calcium content in the interlayer space with the calcium concentrations. Sodium and potassium are taken up in the interlayer space preferentially at low calcium concentrations and thus by low Ca/Si C S H. Aluminium uptake in C S H increases strongly at higher aluminium concentrations in the solution. At low Ca/Si aluminium substitutes silica in the bridging position at Ca/Si. > 1 aluminium is bound in TAH. Recently developed ther…
Accelerated Light-Induced Defect Transformation Study of Elkem Solar Grade Silicon
2012
AbstractSolar cells made of silicon feedstock from a metallurgical route must qualify not only the initial efficiency, but must also be comparable to the solar cells made from reference polysilicon on the spectral response after light induced degradation. A detailed comparative study of light induced defects and its impact on cell performance is necessary for both materials. We have studied accelerated light induced degradation (ALID) defect transformation for Elkem Solar Silicon and polysilicon solar cells by selecting wafers from different positions from respective silicon bricks. Active boron-oxygen complexes and iron ions in multicrystalline silicon solar cells have been analyzed, and t…
One pot light assisted green synthesis, storage and antimicrobial activity of dextran stabilized silver nanoparticles.
2014
Background Green synthesis of nanomaterials finds the edge over chemical methods due to its environmental compatibility. Herein, we report green synthesis of silver nanoparticles (Ag NPs) mediated with dextran. Dextran was used as a stabilizer and capping agent to synthesize Ag NPs using silver nitrate (AgNO3) under diffused sunlight conditions. Results UV–vis spectra of as synthesized Ag nanoparticles showed characteristic surface plasmon band in the range from ~405-452 nm. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) studies showed spherical Ag NPs in the size regime of ~50-70 nm. Face centered cubic lattice of Ag NPs was confirmed by powder X-ray diffraction (PXRD…
Silver-loaded nanoparticles affect ex-vivo mechanical behavior and mineralization of dentin
2019
Background: The aim was to evaluate the effect of silver loaded nanoparticles (NPs) application on the triboscopic, crystallographic and viscoelastic properties of demineralized dentin. Polymethylmetacrylate-based NPs and Ag loaded NPs were applied on demineralized dentin. Material and Methods: Treated and untreated surfaces were probed by a nanoindenter to test viscoelasticity, and by atomic force microscopy to test nanoroughness and collagen fibril diameter. X-ray diffraction and transmission electron microscopy through selected area diffraction and bright-field imaging were also used. Results: Dentin treated with Ag-NPs attained the lowest complex modulus, and the highest tan delta value…
Thermal Properties, Raman Spectroscopy and Tem Images of Neutron-Bombarded Graphite
2013
Neutron-irradiated graphite to a total dose of 3.6 × 1016 n cm−2 was studied by DSC, Raman spectroscopy and transmission electron microscopy (TEM). The Wigner energy of neutron-irradiated graphite was 9.5 J/g as measured by DSC; it was released with an exothermal peak at 220°C. The Raman spectroscopy has confirmed the expected effect caused by neutron irradiation of the graphite substrate. The TEM imaging has shown that neutron-irradiated graphite can be effectively exfoliated by sonication in comparison to pristine graphite, which under similar conditions does not exfoliate at all. The interstitial Frenkel defects in neutron-irradiated graphite are intercalated between the graphene layers …
Determination of the Boron/Lead Ratio in Ceramic Materials Based on Electrochemical Quartz Crystal Microbalance
2004
A method for quantitatively determining the relationship boron/lead in ceramic materials is presented. It is based on the attachment of microsamples of ceramic frits to an electrochemical quartz crystal microbalance (EQCM). After a reductive deposition step in the � 0.25 to � 0.85 V (vs. AgCl/Ag) potential range, well-defined stripping peaks are recorded in 0.10 M NaCl plus 0.10 M mannitol. The deposition of boron and lead from suspensions of solid materials, and its subsequent oxidative dissolution can be monitorized at the EQCM. The quotient between the maximum mass gain and the corresponding charge passed enables for a direct quantitation of the boron/lead molar ratio in ceramic material…