Copolymerization of n-Butyl Acrylate with Methyl Methacrylate and PMMA Macromonomers: Comparison of Reactivity Ratios in Conventional and Atom Trans…
1999
The reactivity ratios of n-butyl acrylate (nBuA) with methyl methacrylate (MMA) and ω-methacryloyl-PMMA macromonomers (MM) in conventional and atom transfer radical copolymerization (ATRP) have been determined. For the copolymerization of nBuA with MMA, good agreement of the ratios is observed between conventional and controlled radical copolymerization, indicating that chemoselectivities in both processes are similar. The relative reactivity of the MM (1/rnBuA) in conventional copolymerization is significantly lower than that of MMA. It depends on the concentration of the comonomers but is not significantly influenced by the length of the MM. At high concentrations the relative reactivity …
Mechanism of Anionic Polymerization of (Meth)acrylates in the Presence of Aluminum Alkyls, 6. Polymerization of Primary and Tertiary Acrylates
1998
The kinetics of the polymerization of n-butyl acrylate initiated by lithiated ester enolates in the presence of aluminum alkyls was investigated in toluene and in toluene/Lewis base mixed solvents at −78 °C. In pure toluene, curved time−conversion plots, incomplete monomer conversion, and broad molecular weight distributions (Mw/Mn ≈ 2) are observedin the absence of aluminum alkyls the molecular weight distributions are significantly broader (Mw/Mn > 14). High monomer conversions and narrower molecular weight distributions (Mw/Mn ≈ 1.5) are obtained when using Lewis bases (e.g., methyl pivalate) as cosolvents. The polymerization of tert-butyl acrylate rapidly reaches full monomer conversion…
Kinetics and mechanism of group transfer polymerization of N-butyl acrylate catalyzed by Hgl2 /(CH3 )3 Sil in toluene
1994
The group transfer polymerization (GTP) of n-butyl acrylate (nBuA) using 1-methoxy-1-(trimethylsiloxy)-2-methyl-1-propene (MTS) as an initiator, mercuric iodide (HgI2) as a catalyst in toluene at room temperature gives a very good control of molecular weight and narrow molecular weight distribution. (Mw/Mn < 1.2). Kinetic studies in this system reveal that this reaction is rather slow, half-lives being in the range of hours. The kinetic order of the apparent rate constant of propagation with respect to initiator and catalyst concentrations were found to be near to unity. However, the first-order time-conversion plots exhibit considerable induction periods. Upon addition of trimethylsilyl io…
Synthesis and solution properties of star-shaped poly(tert-butyl acrylate)
2000
A series of star polymers consisting of poly(tert-butyl acrylate) arms and an ethyleneglycol dimethacrylate (EGDMA) microgel core were synthesized using anionic polymerization. The effect of various parameters (precursor length, ratio [[EGDMA]/[Initiator], reaction time, and overall concentrations) on the average number of arms was investigated. Molecular weights were determined using GPC coupled with an online viscometer and MALLS. The exponents for the relation between intrinsic viscosity or radius of gyration and molecular weight, respectively, are extremely low, indicating that the dimensions of the star polymers only slightly increase with the number of arms. After a certain number of …
Cure behaviour of epoxy resin matrices for carbon fibre composites
1999
The cure behaviour of two resin formulations (with high and low curing agent content respectively) of an epoxy resin system, used as matrix for carbon fibre composites, was studied through calorimetric analysis. The aim of this work is to investigate the kinetics of this specific epoxy system in order to be able to choose a proper set of processing parameters which will give good composite material properties. The shape of the conversion curves gives evidence of the differences in the cure kinetics of the two systems. Furthermore, the values of the activation energies were determined both for formulation in the conversion range where vitrification occurs, following a phenomenological approa…
Airborne bio-aerosols and noise in a dry waste treatment plant in Pietarsaari, Finland
2001
Ewapower Ltd in Pietarsaari, Finland produces pellets from paper and plastic waste for burning. During 1998 and 1999, several measurements were made to determine the dust, particle, microbe and endotoxin concentrations, and also the noise level in the hall where the waste is received and pre-crushed. The noise level exceeded the Finnish recommended level of 85 dBA. The dust and the particle concentrations were low, but the microbe concentrations, especially in the summer and in the autumn, were at a level which may be harmful to health. The total concentration of microbes (both dead and alive) was high - approximately 4.8 million particles m-3. The concentrations of endotoxins was high in …
Formation of supramolecular aggregates by hydrogen bonding based on bispyrimidine and bisbarbituric acid
1997
Hydrogen bonds between bispyrimidine and bisbarbituric acid in equal molar ratio can lead to the formation of supramolecular aggregates. This is established by TEM, IR and DSC measurements. Additionally, WAXS pattern showed that the aggregate is of laminar structure. Both the hydrolysis of this system and termination of the aggregate's growth were studied.
Dynamic Mechanical Behavior Analysis of Flax/Jute Fiber-Reinforced Composites under Salt-Fog Spray Environment
2020
Over the last decades, natural fiber-reinforced polymer composites (NFRPs) gained great attention in several engineering fields thanks to the reduction of the environmental impact and the end-of-life cost disposal. Unfortunately, the use of NFRPs is limited, mainly due to their weak resistance against humid environments. Since limited literature is available about the evolution of the dynamic mechanical response of NFRPs under aggressive environments, this paper aims to investigate the damping properties of flax, jute and flax/jute epoxy composites exposed to salt-fog up to 60 days. Furthermore, sodium bicarbonate fiber treatment was performed to improve the composites&rsquo
The influence of the nature of the surface oxide on the adhesive fracture energy of aluminium-bonded joints as measured by T-peel tests
2008
Abstract Modification of aluminium alloy substrates microstructure and morphology by depositing new oxide layers on top of the metal surface has been investigated, with the aim of improving adhesion. The effect of treating the metal with boiling water or immersing it in a cerate bath has been studied by means of electron microscopy, contact angle measurements and peeling tests. The formation of pseudoboehmite layers or cerium conversion coatings both led to an increase in joint's adhesive fracture energy and more durable adhesive bonds with respect to joints obtained with “mechanically grinded only” substrates. Differences in the performance of the bonded joints has been discussed in terms …
Organo-catalyzed synthesis of aliphatic polycarbonates in solvent-free conditions
2012
A new efficient and expeditious route to the synthesis of aliphatic polycarbonates, in solvent-free conditions and using 1-n-butyl-3-methylimidazolium-2-carboxylate (BMIM-2-CO2) as a catalyst precursor, is described. The protocol consists of a two-step polymerization process involving the transesterification of dimethyl carbonate (DMC) with linear alkane diols and leading to high molecular weight homopolymers. The reaction went to completion quantitatively with the liberation of methanol as the only by-product. The in situ formation of N-heterocyclic carbene species resulting from BMIM-2-CO2 decarboxylation is suggested to be a key feature of the condensation process. The protocol was then …