Thermoelectric properties of Sr_3GaSb_3 – a chain-forming Zintl compound
2012
Inspired by the promising thermoelectric properties in the Zintl compounds Ca_3AlSb_3 and Ca_5Al_2Sb_6, we investigate here the closely related compound Sr_3GaSb_3. Although the crystal structure of Sr_3GaSb_3 contains infinite chains of corner-linked tetrahedra, in common with Ca_3AlSb_3 and Ca_5Al_2Sb_6, it has twice as many atoms per unit cell (N = 56). This contributes to the exceptionally low lattice thermal conductivity (κ_L = 0.45 W m^(−1) K^(−1) at 1000 K) observed in Sr_3GaSb_3 samples synthesized for this study by ball milling followed by hot pressing. High temperature transport measurements reveal that Sr_3GaSb_3 is a nondegenerate semiconductor (consistent with Zintl charge-coun…
Electrical Transport Properties of Lead−Free (Na0.5Bi0.5)1-xBaxZr0.04Ti0.96O3Ceramics (x = 0.06, 0.085, 0.1)
2011
Lead-free ceramics (Na0.5Bi0.5)1-xBaxZr0.04Ti0.96O3 were prepared by solid phase hot pressing sintering process. Density values of obtained samples are higher than 95% of the theoretical ones. Samples with x = 0.06, 0.085 and 0.1 were investigated in the present work. For these samples both ac and dc electric conductivity were studied. A low frequency (100 Hz-100 kHz) ac conductivity obeys the power law, characteristic for disordered materials. The dc conductivity has a thermally activated character. A barrier hopping model is found to explain the mechanism of charge transport in these materials. The (Na0.5Bi0.5)1-xBaxZr0.04Ti0.96O3 system is expected to be a new and promising candidate for…
Direct observation of polar nanostructures in PLZT ceramics for electrooptic applications
2004
ABSTRACTTransparent Pb1-yLay(Zr1-xTix)1-y/4O3(PLZT, y=0.0975, x=0.35) ceramics prepared via hot pressing techniques were studied via piezoelectric force microscopy (PFM). Clear piezoelectric contrast is observed in a cubic relaxor phase indicating spatial distribution of polarization with an average cluster size of about 50 nm. The irregular polarization pattern is associated with the formation of a glassy state, where random electric and stress fields are responsible for the disruption of the long-range ferroelectric order. Local poling of the ceramics resulted in the formation of a stable micron-size domain that could be continuously switched under varying dc bias (local hysteresis loop).…
High temperature oxidation of higher manganese silicides
2021
Abstract The oxidation kinetics and mechanisms of higher manganese silicides (HMS) MnSi1.75, MnSi (1.75-x)Gex, MnSi(1.75-x)Alx (with x = 0.005 and 0.01)were studied and the effects of densification methods and dopant concentration discussed. Oxidation experiments were conducted using thermogravimetry (TGA), while post characterization with X-ray Photoelectron Spectroscopy (XPS) and Scanning Electron Microscope (SEM) showed that spark plasma sintering (SPS) is a better densification method than hot pressing (HP). Except for undoped HMS, HMS doped with 0.5at% Ge had the lowest oxidation rate. Stable formation of a SiO2 protective layer was the main reason for improved oxidation resistance in …
Experimental analysis and micromechanical models of high performance renewable agave reinforced biocomposites
2017
Abstract The present work deals with the experimental study of high performance biocomposites reinforced with optimized agave fibers, as well as the successive implementation of reliable micromechanical models that can be used at the design stage. In detail, systematical experimental analyses performed on biocomposites with epoxy or PLA matrix, have permitted to highlight that for short fibers biocomposites the reinforcing leads to a significant improvement of the matrix stiffness, whereas the particular damage mechanism based essentially on the matrix failure with consequent tensile failure of the fibers aligned with the applied load, does not allow to obtain an actual reinforcing of the m…
Effect of annealing treatment on the persistent luminescence of Y3Al2Ga3O12:Ce3+,Cr3+,Pr3+ ceramics
2020
Abstract The Y3Al2Ga3O12:Ce3+,Cr3+,Pr3+ (YAGG) persistent luminescent ceramics were sintered in static air (without airflow) and followed by hot isostatic pressing (HIP) treatment. The low aggregated and relatively narrow particle-size distributed starting powders, with the particle size of about 50 nm, were synthesized by using Pechini method and then annealed at 900 °C for 16 h in static air. Compared to nano-phosphors, the ceramics exhibited more intense and longer persistent luminescence (PersL). The photoluminescence and PersL spectra were found to have a similar shape, indicating that the emitting centers for photoluminescence and PersL processes were same. The intense Ce3+ and Cr3+ b…
PLZT—Synthesis, sintering and ceramics microstructure
2006
Abstract Producing of PLZT powders by original two-stage co-precipitation method from mixed solution of inorganic salts ZrOCl 2 ·8H 2 O, TiCl 4 , La(NO 3 ) 3 ·6H 2 O, Pb(NO 3 ) 2 , was carried out. The sequence of phases formed during PLZT synthesis has been studied by X-ray and DTA analysis. Ceramic samples were prepared by two-stage hot-pressing technology. Dielectric, ferroelectric and optical properties have been measured. Ceramic microstructures were studied by SEM with energy dispersive analytical capability (EDX). The fine-grained microstructure was quite uniform with the average grain size of 5–7 μm, without internal or grain boundary porosity. The optical transmittance of ceramic p…
Microstructure-oxidation resistance relationship in Ti3AlC2 MAX phase
2020
International audience; Spark Plasma Sintering and Hot Isostatic Pressing were used to synthesize coarse-grained and fine-grained Ti3AlC2 specimens. Moreover, Spark Plasma Sintering processing parameters were modified in order to vary the TiC, Al2O3 and TixAly impurity and the porosity contents in the fine-grained samples. The influence of the Ti3AlC2 microstructure on the oxidation resistance was assesed. It is demonstrated that the grain size can drastically modify the oxidation resistance. The higher density of grain boundaries, in fine-grained specimens, increases the number of Al diffusion paths and leads to the formation of a protective alumina scale. In coarse-grained sample, Al diff…
Consolidation and densification mechanisms of copper powder during Spark plasma sintering (SPS)
2015
Spark plasma sintering is a manufacturing process that leads to dense materials with fine microstructures. SPS combines heating and uniaxial load as well as the Hot Pressing (HP) process but the material is heated using a pulsed current. The phenomena occurring during SPS are not fully understood and are still an open point: -Which densification and consolidation mechanisms are involved during SPS? -Why is sintering by SPS more efficient than sintering by traditional ways such as HP? –Does electrical current modify the sintering mechanisms? The aim of this work is to answer these questions in the case of spherical copper powder (from 10 to 50 µm). Comparisons between SPS and HP were perform…
Modeling of yttrium, oxygen atoms and vacancies in γ-iron lattice
2011
Abstract Development of the oxide dispersion strengthened (ODS) steels for fission and fusion reactors requires a deep understanding of the mechanism and kinetics of Y 2 O 3 nanoparticle precipitation in the steel matrix. Therefore, it is necessary to perform a large-scale theoretical modeling of the Y 2 O 3 formation. In the current study, a series of first-principles calculations have been performed on different elementary clusters consisting of pair and triple solute atoms and containing: (i) the Y–Fe-vacancy pairs, (ii) the two Y atoms substituted for Fe lattice atoms and (iii) the O impurity atoms dissolved in the steel matrix. The latter is represented by a face-centered cubic γ-Fe si…