Structural properties of core and surface of silica nanoparticles investigated by Raman spectroscopy
2013
We studied the experimental Raman spectra of various commercial silica nanoparticles of average diameter from 7 to 40 nm and specific surface from 50 to 380 m^2/g. We found that the peculiarities of the particles Raman spectra systematically depend on their specific surface. In detail, the peak position of the R band at about 440 cm ^-1 shifts towards high wavenumbers following an almost linear dependence on the specific surface. Similarly, the amplitudes of the D1 and D2 bands, at about 495 and 605 cm ^-1, respectively, increase linearly with the same quantity. Our results are interpreted in the frame of the shell model for the nanoparticles clarifying that the network of the core of the n…
Thioflavin-T doped silica nanoparticles by basic-catalyzed sol-gel synthesis
2014
We developed a basic-catalyzed sol-gel procedure that allows to synthesize silica nanoparticles functionalized with Thioflavin-T (ThT). During the synthesis, the formation of the doped silica nanoparticles was monitored by absorbance spectra indicating that the catalyst does not cause the total hydroxylation of the dye. Fluorescence measurements carried out on the ThT doped silica nanoparticles proved the attachment of ThT on silica and Raman spectroscopy provided information about the dye structure.
Visible luminescence of nanosilica: slow and fast contributions
2010
Luminescence properties induced by sintering of silica nanoparticles
2014
The effect of sintering on the optical properties of silica nanoparticles, a mean diameter of ~14 nm, are investigated by absorption and luminescence experiments. The sintering is induced by a thermal treatment of 1000 °C for 272 hours; after that the sample is transparent, and emits a bright luminescence under UV excitation. Time resolved photoluminescence spectra excited by a tunable laser source allows to evidence four bands around 2.0 eV, 2.4 eV, 2.7 eV and 3.4 eV, peculiar to defects induced by the sintering.
Supercooled Water Confined in a Silica Xerogel: Temperature and Pressure Dependence of Boson Peak and of Mean Square Displacements
2013
A silica xerogel can be obtained from an alcoxide precursor (TMOS, tetramethylortosilcate) via the sol-gel method: TMOS hydrolysis and subsequent polycondensation yields a solid, disordered, porous SiO2 matrix (average pore dimensions ~20Å). Inside the pores water is trapped and the hydration level h=gr[H2O]/gr[SiO2] can be easily controlled. The presence and temperature dependence of the boson peak (BP) in xerogel confined supercooled water was studied with inelastic neutron scattering (spectrometer IN6 at ILL, Grenoble) in xerogel samples having h=0.4 and h=0.2. After careful subtraction of the contributions arising from the matrix and from quasi-elastic scattering, the BP contribution wa…
Paramagnetic germanium-related centers induced by energetic radiation in silica based devices
2009
In-situ observation of β-ray induced optical absorption in a-SiO2: radiation darkening and room temperature recovery
2008
The structural disorder of a silica network probed by site selective luminescence of the nonbridging oxygen hole centre
2011
We studied the inhomogeneous distribution of the luminescence band associated with the nonbridging oxygen hole centre in silica through site selective excitation/detection of the zero phonon line by a tunable laser source. Defects induced in the bulk of synthetic samples by γ and β exposure exhibit an increase of the inhomogeneous width from 0.071 to 0.086 eV on increasing the irradiation dose from 2 × 10(6) to 5 × 10(9) Gy. We also investigated two defect variants stabilized at the surface of the silica nanoparticles, (≡ Si-O)3 Si–O* and (≡ Si-O)2(H-O)Si-O*, whose inhomogeneous width was measured to be 0.042 eV and 0.060 eV, respectively. These results can be accounted for by the structura…