Molecular Mass Distribution of Lignin from the Alkaline Pulping of Hardwood, Softwood, and Wheat Straw
2012
Abstract The behavior of lignin during kraft (hardwood, softwood, and wheat straw) and soda-AQ (wheat straw) pulping was studied, mainly in terms of delignification degree and molecular mass distribution (MMD). In the initial delignification phase (at 140°C for 15–60 min), a prominent part of the dissolved softwood kraft lignin (18–25 g/L, MM mostly > 3,000 Da) was found in the liquid phase of chip cavities, rather than in the external bulk black liquor (5–7 g/L, MM mostly < 3,000 Da). The maximum weight average MM values ( w) of the soluble lignin under conventional cooking conditions were detected for the kraft softwood (4,100 Da), and kraft birch (3,400 Da) when the degree of delignifica…
CHEMICAL PULPING. Oxidative degradation of AOX in softwood-based kraft mill effluents from E C F bleachin g
2012
Abstract Softwood-based kraft mill bleaching effluents from the initial bleaching stages D0 and E1 (the bleaching sequence being D0E 1D 1 E2D2) were treated by the oxidative Fenton method (H20rFeS04) to decompose organic pollutants contammg adsorbable organic halogens (AOX). Experiments designed using the Taguchi method were applied to predict the process conditions that would result in a cost-effective and adequate removal of AOX. In addition to the composition and concentration of the reagents (H202 and Fe2+), the main process parameters selected were temperature and reaction time, while pH was adj usted to an approximate value of 4 (the volumetric ratio of the mixed effluents D0:E 1 was …
A LASER-INDUCED FLUORESCENCE (LIF) METHOD FOR MONITORING OXYGEN–ALKALI DELIGNIFICATION OF SOFTWOOD KRAFT PULP
2002
ABSTRACT A laser-induced fluorescence (LIF) method for monitoring the oxygen–alkali delignification of pine (Pinus sylvestris) kraft pulp was tested. The fluorescence intensity of the effluent was found to increase systematically during treatment as the lignin content of the pulp decreased. This emission method, compared, for example, to a UV/Vis absorption method, seems to have potential for large-scale applications. Owing both to the complex chemical nature of the effluent from oxygen–alkali delignification and to the complex nature of the fluorescence method, further work on this method is needed before it can be used for industrial purposes.
Combustion behavior of kraft black liquor droplets from hot water pretreated hardwood and softwood chips
2016
This paper describes the combustion behavior of birch and spruce kraft black liquors obtained from an integrated forest biorefinery concept in which a hot water extraction of chips was performed before pulping. This pretreatment, aiming mainly at the recovery of various hemicellulose-derived materials, increased the concentrations of lignin and hydroxy acids in black liquors, compared with those in the reference black liquors without any process modification. On the other hand, the pretreatment decreased the concentrations of volatile acids and other organics (extractives and hemicellulose residues). Because of these characteristic changes, the total burning times (pyrolysis time plus char …
FTIR Monitoring of Chemical Changes in Softwood During Heating
2000
Abstract A multivariate chemometric method for monitoring the mass loss of Scots pine (Pinus sylvestris) and Norway spruce (Picea abies) by IR spectroscopic determination of chemical changes occurring during the heat treatment (160 - 260 °C, 2 - 8 h) of these wood materials was developed. The method was based on the handling of FTIR data on treated and untreated wood powder samples by the partial least squares (PLS) method. In addition, unknown samples (treated and untreated pine and spruce) were classified into separate groups by the principal component analysis (PCA) method. The chemical changes occurring in the wood samples during heating were also briefly discussed.
Thermochemical behavior of Norway spruce ( Picea abies ) at 180-225 °C
2002
Norway spruce (Picea abies) was heated for 2–8 h in the temperature range 180–225 °C, under a steam atmosphere. The chemical analyses of the treated feedstock samples indicated that during heating (total mass loss 1.5–12.5% of the initial DS) carbohydrates (hemicelluloses and cellulose) were clearly more amenable to various degradation reactions than lignin. In addition, major water-soluble products released from the feedstock material during the treatments were classified into several compound groups and changes in the relative mass portion of these groups were monitored by GC during a separate experiment.
Solid state 13C-NMR methodology for the cellulose composition studies of the shells of Prunus dulcis and their derived cellulosic materials.
2020
Lignocellulosic fibers and microcellulose have been obtained by simple alkaline treatment from softwood al- mond shells. In particular, the Prunus dulcis Miller (D.A.) Webb. was considered as a agro industrial waste largely available in southern Italy. The materials before and after purification have been characterized by 13C CPMAS NMR spectroscopy methodology. A proper data analysis provided the relative composition of lignin and holo- cellulose at each purification step and the results were compared with thermogravimetric analysis and FT-IR. To value the possibility of using this material in a circular economy framework, the fibrous cellulosic material was used to manufacture a handmade c…
Behavior of carbohydrate-based material in black liquor during heating
2004
One industrial softwood Kraft black liquor was heat-treated (at 175 ?C and 190 ?C for 15-60 min) together with laboratory-made soda-AQ (wheat straw and reed canary grass) and Kraft (reed canary grass) black liquors (at 190 ?C for 30 min). The feedstock black liquors were characterized with respect to their polysaccharide (mainly xylem) and aliphatic carboxylic acid contents before and after the heat treatments. It was noted that, due to the higher amount of polysaccharides in the non-wood black liquors (8.2-16.6% of d.s) compared to that in the softwood black liquor (1.4% of d.s), the heat treatment in the former case resulted in a 5-30% increase in the amount of aliphatic acids formed by v…
Chemical Pretreatments of Wood Chips Prior to Alkaline Pulping - A Review of Pretreatment Alternatives, Chemical Aspects of the Resulting Liquors, an…
2015
The chemical industry is being forced to evaluate new strategies for more effective utilization of renewable feedstocks to diminish the use of fossil resources. In this literature review, the integration of both acidic and alkaline pretreatment phases of hardwood and softwood chips with chemical pulping is discussed. Depending on the pretreatment conditions, high-volume sulfur-free fractions with varying chemical compositions can be produced. In case of acidic pretreatments, the major products include carbohydrates (mono-, oligo-, and polysaccharides), whereas under alkaline (i.e., aqueous NaOH) pretreatment conditions, the sulfur-free fractions of aliphatic carboxylic acids, lignin, and ex…