Comparative study of the luminescence properties of macro- and nanocrystalline MgO using synchrotron radiation
2013
MgO nano-powder with an average crystallite size of nanoparticles ranging 10-15 nm was synthesized using the extractive-pyrolytic method and was studied by room temperature VUV spectroscopy under synchrotron radiation excitation. Comparative analysis of their luminescent properties with that of mac- rocrystalline powder analogues and an MgO single crystal, grown by the arc-fusion method, has been per- formed under excitation by pulsed VUV synchrotron radiation. Special attention was paid to VUV spectral range, which is not reachable with commonly used lamp and laser sources. A considerable blue shift of about 0.3 eV in the excitation spectra of 2.95 eV emission band, was revealed in nanocry…
EPR and optical spectroscopy of neutron-irradiated Gd3Ga5O12 single crystals
2020
Abstract In this paper, we have performed comparative analysis of EPR, optical absorption (OA) and luminescence spectra for a series of Gd3Ga5O12 (GGG) single crystals irradiated with fast neutrons with fluencies varied from 1016 to 1020n/cm2. In a crystal irradiated with the maximum neutron fluence, the EPR spectra demonstrated the formation of several paramagnetic defects. In particular, EPR spectrum shows a strong resonance at (effective) g ≈ 1.4 with practically isotropic behavior in the crystal rotation around the [1 1 1] direction (magnetic field being perpendicular to [1 1 1]) and several weaker lines in the g ≈ 1.1–2.6 region, which show more pronounced angular dependences. While th…
Depth profiles of damage creation and hardening in MgO irradiated with GeV heavy ions
2019
This work has been performed within the framework of the EUROfusion Enabling Research project: ENR-MFE19.ISSP-UL-02 “Advanced experimental and theoretical analysis of defect evolution and structural disordering in optical and dielectric materials for fusion applications”. The views and opinions expressed herein do not necessarily reflect those of the European Commission.
Influence of Sr addition on structural, dielectric and Raman properties of Na0.5Bi0.5TiO3ceramics
2016
ABSTRACTLead free (Na0.5Bi0.5)1-xSrxTiO3 (x = 0, 0.01 and 0.02) ceramics were produced by a conventional solid-state sintering method. X-ray diffraction analysis shows that the obtained samples possess the perovskite structure with rhombohedral symmetry. The microstructure study shows a dense structure, in agreement with the relative density (above 97%). Dielectric analysis revealed the diffuse character of the electric permittivity anomalies and their shift to a lower temperature range after Sr doping of NBT. The Raman spectra are similar for all samples in agreement with the X-ray diffraction data. The possible origin of the observed effects was discussed.
Raman spectra and anomalies of dielectric properties and thermal expansion of lead-free (1−x)Na0.5Bi0.5TiO3-xSrTiO3 (x = 0, 0.08 and 0.1) ceramics
2016
ABSTRACTThermal expansion, Raman and dielectric properties of the lead-free (1−x)Na0.5Bi0.5TiO3-xSrTiO3 (x = 0, 0.08 and 0.1) ceramic solid solutions, fabricated by the conventional solid-state reaction method, were investigated. The Sr-doping results in an increase of the dielectric permittivity, broadening of the permittivity maximum, enhancement of the relaxation near depolarization temperature, broadening of the Raman bands and shift of all anomalies toward lower temperatures. The observed effects are attributed to an increase of the degree of cationic disorder and enhancement of the relaxor-like features. Anomalies in the thermal expansion strain were observed at the temperatures corre…
Dielectric, thermal and Raman spectroscopy studies of lead-free (Na0.5Bi0.5)1−xSrxTiO3 (x = 0, 0.04 and 0.06) ceramics
2016
ABSTRACTLead-free (Na0.5Bi0.5)1−xSrxTiO3 (x = 0, 0.04 and 0.06) ceramics with relative densities above 97% were prepared by solid-state synthesis process. Their dielectric, thermal and Raman properties were studied. X-ray diffraction analysis shows perovskite structure with rhombohedral symmetry at room temperature. Sr doping of Na0.5Bi0.5TiO3 (NBT) results in an increase of the dielectric permittivity, diffusing of the permittivity maximum and its shift toward lower temperatures. The temperature of the rhombohedral–tetragonal phase transition indicated by the differential scanning calorimetry (DSC) peak and relaxational dielectric anomaly near the depolarization temperature are also shifte…
Single crystal-like thin films of blue bronze
2021
Abstract Pulsed laser deposition technique was employed to grow thin films of K 0.3 M o O 3 on A l 2 O 3 (1-102) and S r T i O 3 (510) substrates. Structural and imaging characterization revealed good quality films with well oriented grains of few microns in length. Both non-selective (transport) and order-selective (femtosecond pump-probe spectroscopy) probes revealed charge density wave properties that are very close to those of the single crystals. The films exhibit metal-semiconductor phase transition in resistivity, pump-probe data show phase transition at the same temperature as the single crystal and the threshold for the photo-induced phase transition is approximately the same as in…
Dielectric behaviour of BaTi1-xZrxO3ceramics obtained by means of a solid state and mechanochemical synthesis
2016
ABSTRACTIn this study the comparison of dielectric behaviour of BaTi1-xZrxO3 (BTZx) ceramic samples prepared by means of a solid state and mechanochemical synthesis was presented. A single phase of perovskite structure was identified in the samples at room temperature. No significant impurities were detected in an EDS spectrum and the samples had a good stoichiometric ratio. The morphology of the investigated samples was characterized by a scanning electron microscopy (SEM). The investigation of dielectric properties of the BTZx samples within the temperature range from 140 K to 600 K was performed by means of a dielectric spectroscopy method at the frequency ranging from 0.1 Hz to 10 MHz. …
Compact setup for spin-, time-, and angle-resolved photoemission spectroscopy.
2020
Review of scientific instruments 91(6), 063001 (2020). doi:10.1063/5.0004861
Defect-induced blue luminescence of hexagonal boron nitride
2016
Abstract Native defect-induced photoluminescence around 400 nm (blue luminescence - BL) was studied in hBN materials with different size and various origins. The following spectral characterizations were used: spectra of luminescence and its excitation, luminescence dependence on temperature, luminescence kinetics, optically stimulated luminescence and infrared absorption. It was found, that the BL is characteristic for all these materials, which were studied. The BL forms a wide, asymmetric and phonon-assisted emission band at 380 nm. This luminescence can be excited either through the exciton processes, or with light from two defect-induced excitation bands at 340 nm and 265 nm. It was fo…