Electronic properties and corrosion resistance of passive films on austenitic and duplex stainless steels
2018
Abstract Passive films were grown at constant potential in acidic (pH∼2) and alkaline (pH∼13) solutions on chromium, AISI 304L, AISI 316L and Duplex stainless steels. Passive films on chromium grow following a high field mechanism considering the presence of dissolution phenomena. According to the photoelectrochemical characterization, passive films on Cr have a bandgap of 3.4 eV when formed in acidic solution, and of 2.4 eV when formed in alkaline solution due to the formation of Cr(OH)3. These films result to be poorly stable against anodic dissolution due to a very anodic flat band potential. Conversely, impedance and photoelectrochemical measurements proved that passive films on stainle…
Seismic Performance of Earthquake-Resilient RC Frames Made with HSTC Beams and Friction Damper Devices
2021
Seismic behavior of RC frames with hybrid steel-trussed concrete beams is affected by panel zone damage due to a large amount of longitudinal reinforcement. Here the seismic efficiency of innovative frames characterized by friction damper devices (FDDs) at beam-to-column connections is compared against traditional frame. Three configurations are investigated: FDDs alone; FDDs with column-to-foundation connections having preloaded threaded bars and disk springs; FDDs with self-centering friction devices. Non-linear analyses show that FDDs alone prevent plastic hinge formation at beam ends and beam–column joint damage. FDDs with self-centering friction devices effectively limit both peak and …
Some comments on the experimental behavior of FRC beams in flexure
2008
In the present paper the experimental results, recently obtained by the authors, regarding the monotonic and the cyclic flexural response of normal and high-strength concrete beams reinforced with steel bars and discontinuous fibers, are shown. From the experimental results, all referred to low values of shear-to-depth ratios, it emerges clearly that the shear failure is brittle especially under cyclic actions highlighting the role of the fibers in the flexural behavior of the beams. The cyclic action produces a significant decay in the stiffness and in the strength capacity of the beams, and the addition of fibers reduces these negative effects. Form theoretical point of view good agreemen…
Magnetic Field and Short-Circuit Reactance Calculation of the 3-Phase Transformer with Symmetrical Amorphous Core
2006
Magnetically symmetric, 3- phase transformer has been analysed. For the two variants of the windings, the calculation results have been compared with the measured ones. Magnetic flux density components were calculated in and out of the core. The flux distribution and short-circuit reactance have been verified experimentally and a good agreement has been obtained.
Compressive response of substandard steel-jacketed RC columns strengthened under sustained service loads: From the local to the global behavior
2018
Abstract This paper presents an experimental investigation on substandard partially steel jacketed RC columns strengthened under sustained loads and loaded until failure. The aim of the study is to compare the compressive response of preloaded columns with respect to the tests without preload to obtain a more realistic prediction of load-carrying capacity of structural columns after retrofitting under serviceability loads. The influence of the preload level, the delayed contribution of the confining device during the loading process and the time dependent effects are highlighted for the tested specimens. Based on the experimental observations, an analysis-oriented model is proposed for the …
Contribution to the study of physico-chemical properties of surfaces modified by last treatment : application to the enhancement of localized corrosi…
2011
Metallic materials are more and more used in severe conditions with particularly strong request for improving their behavior in aggressive environment and especially over long periods. The objective of this PhD work is to estimate the potentiality of a laser surface melting treatment on the improvement of the stainless steel 304L corrosion resistance, surface treatments by laser can be revisited on the basis of a recent change in the laser technology. In the frame of this work, a nano-pulsed laser fiber was chosen : it allows the treated surface to be melted for few microns in depth, followed by an ultra-fast solidification occuring with cooling rates up to 1011 K/s. The combination of thes…
Degraded Gerber Saddles in RC Bridges
2023
Sudden failure of reinforced concrete (RC) or prestressed concrete (PC) Gerber saddles of bridges and viaducts has occurred all around in the word in the last few years due to corrosion of steel bars. The danger of sudden and brittle failure is often due to general and pitting corrosion of steel bars, concrete crushing, and loss of bond in steel bars. In this paper, the flexural response of reinforced concrete Gerber supports under their self-weight with or without service loads was investigated through determination of the load-deflection response of beams, with the focus on the consequences of pitting corrosion and loss of bond in steel bars. A simplified strut-and-tie model was developed…
Co-deposition and characterization of hydroxyapatite-chitosan and hydroxyapatite-polyvinylacetate coatings on 304 SS for biomedical devices
2019
During the last decades, biomaterials have been deeply studied to fabricate and improve coatings for biomedical devices. Metallic materials, especially in the orthopedic field, represent the most common materials used for different type of devices thanks to their good mechanical properties. Nevertheless, low/medium resistance to corrosion and low osteointegration ability characterizes these materials. To overcome these problems, the use of biocoatings on metals substrate is largely diffused. In fact, biocoatings have a key role to confer biocompatibility features, to inhibit corrosion and thus improve the lifetime of implanted devices. In this work, the attention was focused on Hydroxyapati…
Studio della resistenza alla corrosione di acciai impiegati nell’industria alimentare e delle bevande
2020
In the present study we performed the physico-chemical characterization of passive films grown on different stainless steel grades after long exposure time in hot purified water (HPW). In order to get more insight into dissolution phenomena that can induce rouging on equipment materials typically involved in food and beverage industries, 304L, 316L and a super duplex 2507 SS samples were passivated at the open circuit potential by different immersion times in HPW at 60°C. Photoelectrochemical and Electrochemical Impedance measurements were performed in the attempt to correlate the electronic properties of the passive films (band gap and conductivity type) to their corrosion resistance.
Effect of saliva contamination on bracket failure with a self-etching primer: A prospective controlled clinical trial
2010
Introduction The aim of this study was to evaluate in vivo the effect of saliva contamination at different stages of the bonding procedure on the bond failure rate and the adhesive remaining on teeth after debonding brackets bonded with a hydrophilic self-etching primer (Transbond Plus self-etching primer [TSEP], 3M Unitek, Monrovia, Calif). Methods This was a prospective controlled clinical trial. The sample consisted of 46 patients with similar treatment plans and mechanotherapies. Stainless steel brackets (n = 531) were bonded with TSEP. The patients were divided into 2 groups: contamination with saliva before TSEP application and contamination with saliva after TSEP application. In both…