Mechanical properties and microstructural study of homogeneous and heterogeneous laser welds in α, β,and α + β titanium alloys
2018
International audience; Heterogeneous welding has been investigated for three different couples of titanium alloys: α/α + β, α/β,andα + β/β. Plates of 100 × 60 mm and 1.6 or 1.8 mm thick were welded with a Yb:YAG laser. Tensile tests show that the resistance of the heterogeneous welded specimens was generally controlled by those of the weakest material except for the α + β/β where the ultimate tensile strength was approximately equal to the average value of both materials. In every case, the elongation of the welded sample was found to be smaller than that of the base metals. The rupture generally took place outside the weld metal and was found to be most of the time located in the alloy ha…
Structure and composition heterogeneity of a FeAl alloy prepared by one-step synthesis and consolidation processing and their influence on grain size…
2006
Abstract This paper aims to characterize a bulk dense FeAl (47 at.%) alloy synthesized and consolidated by one-step current-activated pressure-assisted processing of nanocrystalline elemental powders. The end-product was analyzed using a combination of scanning (SEM) and transmission electron microscopies (TEM), electron back-scattering diffraction (EBSD) as well as electron probe microanalysis (EPMA). Special attention was paid to verify the grain size (32–89 nm) previously determined by X-ray diffraction peak profile analysis. It has been found that this material displays equiaxed grains (0.8–4 μm in size) and contains limited structural defects like subgrains and dislocations. The EPMA r…
Single-crystal I h ice surfaces unveil connection between macroscopic and molecular structure
2017
Physics and chemistry of ice surfaces are not only of fundamental interest but also have important impacts on biological and environmental processes. As ice surfaces—particularly the two prism faces—come under greater scrutiny, it is increasingly important to connect the macroscopic faces with the molecular-level structure. The microscopic structure of the ubiquitous ice Ih crystal is well-known. It consists of stacked layers of chair-form hexagonal rings referred to as molecular hexagons. Crystallographic unit cells can be assembled into a regular right hexagonal prism. The bases are labeled crystallographic hexagons. The two hexagons are rotated 30° with respect to each other. The linkage…
Hydrogen influence on the structure and properties of amorphous hydrogenated carbon films deposited by direct ion beam
2008
Abstract The present work provides results for amorphous hydrogenated carbon (a-C:H) films grown by direct ion beam deposition method. Acetylene and its mixtures with hydrogen were used. The films were characterized by Rutherford backscattering spectrometry, elastic recoil detection, Raman spectroscopy, ellipsometry, infrared spectroscopy, and microhardness measurements. These techniques indicated that an admixture of hydrogen yields a lower deposition rate, a higher content of total and bounded hydrogen in the a-C:H films, and a lower film density. The optical and mechanical properties depend on both, hydrogen concentrations in the gas phase and in the films, and show a strong diamond-like…
Optical active centres in ZnO samples
2006
Abstract In recent years, there has been a resurgence in the interest in the use of ZnO (Eg ∼ 3.37 eV) as a material for a wide range of opto-emitter applications spanning visible and short wavelengths. Bulk, thin films and nanomaterials obtained using different synthesis methods have been investigated for optoelectronic and biotechnological device applications. Nominally undoped bulk samples typically present a myriad-structured near-band-edge recombination, mainly due to free/bound excitons and donor–acceptor pair transitions. Furthermore, deep level emission due to intrinsic defects and extrinsic impurities, such as transition metal ions, are commonly observed in different grades of bulk…
Selective area vapor-phase epitaxy and structural properties of Hg1 − xCdxTe on sapphire
1997
Selective area (SA) Hg1 − xCdxTesapphire layers have been grown using the recently developed technique of the vapor-phase epitaxy (VPE) of Hg1 − xCdxTe layers on CdTesapphire heteroepitaxial substrates (HS), which we have called “VPE on HS technique” (Sochinskii et al., J. Crystal Growth 149 (1995) 35; 161 (1996) 195). First, planar CdTe (1 1 1) 5–7 μm thick layers were grown on sapphire (0 0 0 1) wafers by metalorganic vapor-phase epitaxy (MOVPE) at 340°C for 1–2.5 h using dimethylcadmium and di-isopropyltellurium as precursors. Second, CdTe/sapphire mesas were formed using standard photolithography in the form of alternating parallel linear arrays consisting of 500 × 70 μm2 elements. Thir…
Luminescence and structural properties of defects in ion implanted ZnO
2006
ZnO substrates and films were intentionally implanted with rare earth and transition metal ions. The influence of the implantation and subsequent air thermal annealing treatments on the structural and optical properties of ZnO samples were studied by using Rutherford backscattering spectrometry and low temperature photoluminescence techniques. Intraionic Tm-related emission was observed for bulk and ZnO films. Similarly, Eu and Tb-doped ZnO films follow the same trend observed in bulk samples. No intraionic related emission was observed for Eu-doped samples even being the ion in Zn sites and for the Tb-doped samples ion segregation was observed for thermal annealing temperatures above 800 °…
Extracting science from Mössbauer spectroscopy on Mars
2003
[1] Deployment by the Mars Exploration Rovers of backscatter Mossbauer spectrometers offers an incredible opportunity to (1) elucidate the iron mineralogies of rocks, soils, and atmospheric dust and (2) gain insight into the physical event by which the mineralogy came into existence and consequently acquire information having potential for yielding ancient planetary history relevant to broad issues including the question of life. Determining the mineralogy is done by subjecting raw data to reduction algorithms and generating products known as Mossbauer parameters, which are highly characteristic. Mixed mineralogies are treated through deconvolution. Through being able to exploit Mossbauer m…
Effects of heat treatments on the properties of copper phthalocyanine films deposited by glow-discharge-induced sublimation
2006
Copper phthalocyanine films have been deposited by glow-discharge-induced sublimation. The films have undergone postdeposition heat treatments in air at 250 and 290 °C for different times, ranging from 30 min to 14 h. The properties of as-deposited and heated films have been investigated by different techniques in order to determine the effects of heat treatments on the film properties. Fourier transform infrared analysis and UV−visible optical absorption analysis point out a gradual evolution of the film structure from a mixture of α and β polymorphs to the only β polymorph in the sample heated at 290 °C for 14 h. A pronounced decrease of carbon and nitrogen atomic percentages against an o…
Highly textured Gd2Zr2O7 films grown on textured Ni-5at.%W substrates by solution deposition route: Growth, texture evolution, and microstructure dep…
2012
Abstract Growth, texture evolution and microstructure dependency of solution derived Gd 2 Zr 2 O 7 films deposited on textured Ni-5 at.%W substrates have been extensively studied. Influence of processing parameters, in particular annealing temperature and dwell time, as well as thickness effect on film texture and morphology are investigated in details. It is found that a rotated cube-on-cube epitaxy of Gd 2 Zr 2 O 7 //NiW in-plane texture forms as soon as the (004) out-plane texture appears, implying that epitaxial growth dominates the crystallization processes. Thermal energy plays an important role in minimizing the difference of interfacial energy along two directions in the anisotropic…