Properties of the quaternary half-metal-type Heusler alloyCo2Mn1−xFexSi
2006
This paper reports on the bulk properties of the quaternary Heusler alloy Co2Mn1�xFexSi with the Fe concentration x =0,1/2,1. All samples, which were prepared by arc melting, exhibit L21 long-range order over the complete range of Fe concentration. The structural and magnetic properties of the Co2Mn1�xFexSi Heusler alloys were investigated by means of x-ray diffraction, high- and low-temperature magnetometry, Mossbauer spectroscopy, and differential scanning calorimetry. The electronic structure was explored by means of highenergy photoemission spectroscopy at about 8 keV photon energy. This ensures true bulk sensitivity of the measurements. The magnetization of the Fe-doped Heusler alloys …
Crystal growth, structure, magnetic properties and theoretical exchange interaction calculations of Cu2MnBO5
2016
Single crystals of ludwigite Cu2MnBO5 were synthesized by flux growth technique. The detailed structural and magnetic characterizations of the synthesized samples have been carried out. The cations composition of the studied crystal was determined using X-ray diffraction and EXAFS technique, the resulting composition differ from the content of the initial Mn2O3–CuO components of the flux. Magnetic susceptibility measurements and the calculations of the exchange integrals in frameworks of indirect coupling model revealed that monoclinic distortions strongly affect exchange interactions and appearance of magnetic ordering phase at the temperature T=93 K. The hypothesis of the existence of sev…
Zero-field magnetometry based on nitrogen-vacancy ensembles in diamond
2018
Ensembles of nitrogen-vacancy (NV) centers in diamonds are widely utilized for magnetometry, magnetic-field imaging and magnetic-resonance detection. They have not been used for magnetometry at zero ambient field because Zeeman sublevels lose first-order sensitivity to magnetic fields as they are mixed due to crystal strain or electric fields. In this work, we realize a zero-field (ZF) magnetometer using polarization-selective microwave excitation in a 12C-enriched HPHT crystal sample. We employ circularly polarized microwaves to address specific transitions in the optically detected magnetic resonance and perform magnetometry with a noise floor of 250 pT/Hz^(1/2). This technique opens the …
On the Possibility of Miniature Diamond-Based Magnetometers Using Waveguide Geometries
2018
Micromachines 9(6), 276 (2018). doi:10.3390/mi9060276
Spin polarization of magnetoresistive materials by point contact spectroscopy
2003
In the strive to find a straightforward method for determining the spin polarization, the analysis of the Andreev reflection process in point contact junctions has attracted much interest. However, the prerequisite for anevaluation of the transport spin polarization in this scheme is the existence of elastic (ballistic or diffusive) transport, which cannot be assumed a priori. We therefore also include inelastic processes in our analysis and exemplify that thermal effects can have a significant effect on data evaluation. As ferromagnetic samples with a predicted half metallic behavior and comparably low conductivity we used thin films of the double perovskite Sr 2 FeMoO 6 and bulk material …
Generation and characterization of T40/A5754 interfaces with lasers
2014
Laser-induced reactive wetting and brazing of T40 titanium with A5754 aluminum alloy with 1.5 mm thickness was carried out in lap-joint configuration, with or without the use of Al5Si filler wire. A 2.4 mm diameter laser spot was positioned on the aluminum side to provoke spreading and wetting of the lower titanium sheet, with relatively low scanning speeds (0.1 to 0.6 m/min). Process conditions did not play a very significant role on mechanical strengths, which were shown to reach 250-300 N/mm on a large range of laser power and scanning speeds. In all cases considered, the fracture during tensile testing occurred next to the TiAl3 interface, but in the aluminum fusion zone. In a second st…
Corrosion resistance of the FeAlC permanent magnet alloy
1998
Abstract The correlation between corrosion behaviour rate of hard magnetic FeAlC alloys and their microstructure and phase composition is presented. Potentiokinetic polarization curves of the tested material in acid (pH = 1 and 2) and neutral (pH = 7) sulphate solutions have been measured. For open-circuit condition, kinetic curves of etching of the samples in 0.5 M H2SO4 have been determined. The resistance of the tested magnets against atmospheric corrosion has been evaluated using a salt-spray test. The atmospheric corrosion rate is 1.5–2 times slower than that found for Nd-Fe-B type magnets. The FeAlC alloys show good corrosion resistance in neutral environments and corrode at rates…
Beta forging of Ti-6Al-4V: Microstructure evolution and mechanical properties
2013
Titanium alloys are finding an increasing use in the aeronautical field, due to their characteristics of high mechanical properties, lightness and corrosion resistance. Moreover these alloys are compatible with the carbon fibre reinforced plastics that are also finding a wide use in the aeronautical field. On the other hand the use of these alloys implies some drawbacks, for example titanium alloys are often considered more difficult to form and generally have less predictable forming characteristics than other metallic alloys such as steel and aluminum. In this paper was studied both the microstructure evolution and the mechanical properties of a Ti-6Al-4V rolled bar after hot forging. The…
High Temperature Oxidation of TiAl and TiAl8Nb Alloys in Air
2011
Isothermal oxidation of two g-TiAl-based intermetallic alloys: Ti48Al and Ti46Al8Nb alloys was studied in synthetic air at 1073-1223 K for up to 240 hrs. Mass change per unit area for the oxidized samples followed approximately the parabolic rate law. The kp values for the studied temperature interval were in the range from 7.2×10-13 to 1.8×10-11 g2cm-4s-1. The activation energy for oxidation of Ti48Al alloy in air at 1073-1223 K was Ea = 165±12 kJ/mol. Niobium addition to Ti48Al alloy in the amount of 8% increased its oxidation resistance. Structure and chemical composition of the oxidation products, and morphology of the oxidized samples were investigated using XRD, SEM-EDS, and TEM. The …
Soft X-ray photoelectron microscopy used for the characterization of diamond, a-C and CN , thin films
2002
Abstract This article gives an overview about the application of X-ray photoemission electron microscopy (X-PEEM) used for the analysis of carbon thin films. We present the results of an X-ray absorption near edge structure (XANES) study of CVD diamond, a-C and CNx films on Si (100) as well as a defect analysis of a hard disc scratch test. The sp2/sp3 ratio of the carbon films was determined and mapped in the electron micrographs, which show localized defects in the surface.