A DIC-based study of flexural behaviour of roving/mat/roving pultruded composites
2015
Abstract This paper reports a study of the flexural behaviour and resultant failure modes in E-glass/polyester pultruded composites. The digital image correlation (DIC) method is used to estimate the effect of fibre orientation on failure behaviour in thick beams, taking into account the presence of continuous filament mat layer (CFM) in the stacking sequence. In particular, the tests were carried out for specimens with off-axis angle of 0°, 7.5°, 15°, 30°, 45° and 90°. The crack initiation and the failure mechanisms depend on the mutual interaction between the stiffness properties of different areas in the stacking sequence. An influence index (I) was introduced to evaluate the magnitude o…
Digital image correlation analysis of interfacial debonding properties and fracture behavior in concrete
2007
The use of digital image correlation (DIC) as a fracture mechanics tool is described, for two projects currently underway. The goal of the first project is to examine the bond between carbon fiber reinforced polymers (CFRP) and concrete substrates. The second project involves the interfacial transition zone (ITZ) of plain concrete, and the softening and fracture behavior of this region. For both projects, DIC allows for precise measurement of the surface displacements of the deforming materials. The resulting strain data are higher in resolution than is possible with other experimental techniques. For both projects, the DIC results are being used to determine bond constitutive laws, which w…
Quantifying the thermo-mechanical impact of plume arrival on continental break-up
2013
Abstract The arrival of a plume head at Earth's continental lithosphere is often considered to be an important factor for continental break-up. However, the impact of plume impingement on strength and duration of a rift remains unclear. In this study, we quantify the mechanical and thermal influence of a plume (i.e. lithosphere erosion) on continental break-up. To do that we apply the three-dimensional numerical code SLIM3D that features realistic elasto-visco-plastic rheology. We model the thermo-mechanical response of a segment of Earth's lithosphere that is affected both by extension as well as plume-related lithosphere erosion in order to evaluate the influence on the overall force budg…
The lamination machine and laminating as thing-power in early childhood pedagogical practice
2021
This article considers the different ways in which the lamination machine influences early childhood practice. By using Jane Bennett’s notion of ‘thing-power’, we focus on how preschool teachers an...
A comparison among different kinds of stator lamination in tubular linear machines
2016
In this paper the authors perform a comparison among three different stator structures for a Tubular Permanent Magnet Linear Machine. Each structure is characterized by its own lamination which is expected to contribute to the overall performance of the machine. A detailed analysis of the main figures of merit of the three configurations has been carried out in order to identify the configuration with the best characteristics. Significant data such as flux distribution, rated voltage and current, force on the moved and power losses have been compared. The results show that the choice of a mixed stator lamination allows to improve the performance of these machines.
Numerical Analysis of Piezoelectric Active Repair in the Presence of Frictional Contact Conditions
2013
The increasing development of smart materials, such as piezoelectric and shape memory alloys, has opened new opportunities for improving repair techniques. Particularly, active repairs, based on the converse piezoelectric effect, can increase the life of a structure by reducing the crack opening. A deep characterization of the electromechanical behavior of delaminated composite structures, actively repaired by piezoelectric patches, can be achieved by considering the adhesive layer between the host structure and the repair and by taking into account the frictional contact between the crack surfaces. In this paper, Boundary Element (BE) analyses performed on delaminated composite structures …
The Transverse Crack Tension test revisited
2016
Several problems arise when measuring the mode II interlaminar fracture toughness using a Transverse Crack Tension specimen; in particular, the fracture toughness depends on the geometry of the specimen and cannot be considered a material parameter. A preliminary experimental campaign was conducted on TCTs of different sizes but no fracture toughness was measured because the TCTs failed in an unacceptable way, invalidating the tests. A comprehensive numerical and experimental investigation is conducted to identify the main causes of this behaviour and a modification of the geometry of the specimen is proposed. It is believed that the obtained results represent a significant contribution in …
Drilling characteristics and properties analysis of fiber reinforced polymer composites: A comprehensive review
2023
Fiber-reinforced polymer (FRP) composites play a vital role in the production of structural and semi-structural components for engineering applications. The drilling process is a commonly employed machining process for FRP composites to join the FRP structural elements. Usually, the FRP composites possess a heterogeneous nature because of their multi-layered structure, hybridization, and the presence of multi-phase materials. Hence, common problems like delaminations, fuzzing, buckling, cracking, matrix and fiber burning occur during the drilling operations. These problems cause dimensional inaccuracy, poor surface finish, and tool wear and reduce the mechanical strength of the composites. …
An analysis of interface delamination mechanisms in orthotropic and hybrid fiber-metal composite laminates
2007
Abstract The onset and propagation of interlaminar defects is one of the main damage mechanisms in composite materials. This is even more the case when considering layered materials comprising metallic laminae (typically Aluminium) and FRP laminae. Propagation of delamination mainly depends on the initial crack extension and its loading mode. This work presents some results of a combined analytical–numerical–experimental study on the onset and propagation mechanisms regarding interlaminar defects. Two cases have been analysed in particular, the first consisting of a glass-fibre reinforced epoxy resin laminate, and the second consisting of a hybrid laminate where a lamina of aluminium is lay…
Dependence of fracture toughness of composite laminates on interface ply orientations and delamination growth direction
2004
A critical review has been performed of the published experimental research concerning delamination onset and growth in composite laminate interfaces of different lay-ups under single-mode loadings. It was found that, depending on the loading mode and interface lay-up, the traditional fracture toughness characterization by unidirectionally reinforced composite tests can lead to marked under- or overestimation of material resistance to crack growth. Empirical models of fracture toughness as a function of delamination front orientation with respect to reinforcement directions of the adjacent laminae have been validated and their applicability range established.