Early bone healing around implant surfaces treated with variations in the resorbable blasting media method. A study in rabbits.
2010
Objective: this study aimed to histomorphologically and histomorphometrically evaluate the in vivo response to three variations in the resorbable blasting media (RBM) surface processing in a rabbit femur model. Study Design: screw root form implants with 3.75 mm in diameter by 8 mm in length presenting four surfaces (n=8 each): alumina-blasted/acid-etched (AB/AE), bioresorbable ceramic blasted (TCP), TCP + acid etching, and AB/AE + TCP were characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The implants were placed at the distal femur of 8 New Zeland rabbits, remaining for 2 weeks in vivo. After sacrifice, the implants were nondecalcified processed to 30 …
Marginal bone loss in relation to the implant neck surface: An update
2010
A review is made of the publications on the marginal bone loss of implants with a polished neck, rough neck with microthreading, and rough neck without microthreading. A PubMed search was carried out with the following key words: machined neck implant, polished neck implant, marginal bone loss, covering the period between January 1998 and March 2009. Inclusion was limited to those human clinical studies involving a minimum follow-up of 12 months, and registering the level of bone loss from the time of placement of the implant or prosthetic restoration to the end of follow-up. For most of the authors there were no significant differences in marginal bone loss between polished neck and rough …
Effects of a local single dose administration of growth hormone on the osseointegration of titanium implants.
2021
The aim of the present study was to evaluate the effect of different concentrations of growth hormone (GH) on endosteal implant?s surface at the early stages of osseointegration. Sixty tapered acid-etched titanium implants were divided into four groups: i) Collagen, used as a control group; and three experimental groups, where after collagen coating, GH was administered directly to the surface in varying concentrations: ii) 0.265 mg, iii) 0.53 mg, and iv) 1 mg. Implants were placed in an interpolated fashion in the anterior flange of C3, C4 or C5 of 15 sheep with minimum distance of 6 mm between implants. After 3-, 6- and 12-weeks of healing samples were harvested, histologically processed,…
Topographic characterisation of dental implants for commercial use.
2016
Background To characterize the surface topography of several dental implants for commercial use. Material and Methods Dental implants analyzed were Certain (Biomet 3i), Tissue Level (Straumann), Interna (BTI), MG-InHex (MozoGrau), SPI (Alphabio) and Hikelt (Bioner). Surface topography was ascertained using a confocal microscope with white light. Roughness parameters obtained were: Ra, Rq, Rv, Rp, Rt, Rsk and Rku. The results were analysed using single-factor ANOVA and Student-Neuman-Keuls(p<0.05) tests. Results Certain and Hikelt obtained the highest Ra and Rq scores, followed by Tissue Level. Interna and SPI obtained lower scores, and MG-InHex obtained the lowest score. Rv scores followed …
Impact of implant thread design on insertion torque and osseointegration:a preclinical model
2022
Successful osseointegration of endosteal dental implants has been attributed to implant design, including the macro-, micro- and nano- geometric properties. Based on current literature pertaining to implant design, the resultant cellular and bone healing response is unknown when the thread thickness of the implants is increased, resulting in an increased contact area in implants designed with healing chambers. The aim of this study was to evaluate the effect of two implant designs with different thread profiles on the osseointegration parameters and implant stability at 3- and 6-weeks in vivo using a well-established preclinical dog model. A total of 48 type V Ti alloy implants were divided…
A prospective evaluation of zirconia anterior partial fixed dental prostheses: Clinical results after seven years.
2014
Abstract Statement of problem Because of the high mechanical strength of zirconium dioxide, the metal in fixed partial prostheses can now be replaced. However, the material is susceptible to aging or hydrothermal degradation and to chipping of the feldspathic veneer. Purpose The purpose of this prospective study was to evaluate the survival (without failure) and success (survival without any complication or failure) rate and clinical efficacy of anterior zirconia partial fixed dental prostheses. Material and methods Twenty-seven anterior partial fixed dental prostheses of 3 to 6 units were fabricated. All participants were examined after 1 month and 6 months, then annually for 7 years. Resu…
Survival rates of a lithium disilicate-based core ceramic for three-unit esthetic fixed partial dentures: a 10-year prospective study.
2013
Purpose The aim of this prospective study was to evaluate the clinical efficacy and long-term survival rate of three-unit fixed partial dentures (FPDs) made from lithium disilicate-based core ceramic. Materials and methods Twenty-one three-unit FPDs were placed in 19 patients to replace single lost teeth in the esthetic area, following a study protocol that took clinical, esthetic, and radiologic aspects into consideration. Each case was reviewed at 1 week following placement, at 6 months, and then annually for 10 years. Statistical analysis was performed using Kaplan-Meier survival analysis. Results Out of the 19 patients, 14.3% presented reversible postoperative sensitivity. Recession was…
In vitro comparison of the retention capacity of new aesthetic brackets.
1999
Tensile bond strength and bond failure location were evaluated in vitro for two types of aesthetic brackets (non-silanated ceramic, polycarbonate) and one stainless steel bracket, using bovine teeth as the substrate and diacrylate resin as the adhesive. The results show that metallic bracket had the highest bond strength (13.21 N) followed by the new plastic bracket (12.01 N), which does not require the use of a primer. The non-silanated ceramic bracket produced the lowest bond strength (8.88 N). Bond failures occurred mainly between bracket and cement, although a small percentage occurred between the enamel-cement interface with the metal and plastic brackets and within the cement for the …
Retentive strengths of cast gold crowns using glass ionomer, compomer, or resin cement
1998
The retention forces of a newly developed compomer cement (Dyract Cem), a glass ionomer cement (Ketac Cem Aplicap), and a resin cement (F21) were examined.Cemented cast gold crowns were removed along the path of insertion with a Zwick universal testing device. The impact of both a cured and a noncured additional bonding layer that were applied to the inner surface of the crowns was examined across the Dyract Cem group.The mean adhesive strength was measured at 2.36 +/- 0.69 N/mm2 in the Ketac Cem group, at 0.60 +/- 0.28 N/mm2 in the F21 group, and at 1.85 +/- 0.94 N/mm2 in the Dyract Cem group, respectively. The application of an additional bonding layer to the inner surface of the crowns d…
In Vitro Evaluation of the Biological Effects of ACTIVA Kids BioACTIVE Restorative, Ionolux, and Riva Light Cure on Human Dental Pulp Stem Cells
2019
This study aimed to analyze the biological effects of three new bioactive materials on cell survival, migration, morphology, and attachment in vitro. ACTIVA Kids BioACTIVE Restorative (Pulpdent, Watertown, MA, USA) (Activa), Ionolux (Voco, Cuxhaven, Germany), and Riva Light Cure UV (SDI, Bayswater, Australia) (Riva) were handled and conditioned with a serum-free culture medium. Stem cells from human dental pulp (hDPSCs) were exposed to material extracts, and metabolic activity, cell migration, and cell morphology were evaluated. Cell adhesion to the different materials was analyzed by scanning electron microscopy (SEM). The chemical composition of the materials was evaluated by energy-dispe…