Cytotoxicity of Root Canal Filling Materials to Three Different Human Cell Lines
2001
The aim of this study was to investigate the biological compatibility of five root canal sealers (Sealapex, Endion, Super-EBA, Ketac-Endo, and AH Plus) and regular and calcium hydroxide-based gutta-percha in three different human cell lines. Cultures without root canal sealers were used as controls. Cell growth, cell morphology, cell viability, protein content of the cells, and prostaglandin E 2 (PGE 2 ) release were used as parameters to determine the cytotoxicity of the materials. The protein content of the three cell lines—nasal fibroblasts, gingival fibroblasts, and epithelial tumor cells—was significantly reduced (p ≤ 0.001) by all materials tested. Determinations of PGE 2 release show…
Effect of water-jet flossing on surface roughness and color stability of dental resin-based composites.
2019
Background The purpose of this in vitro study was to investigate the effects of water-jet flossing on the color stability and surface roughness of five resin-based composites. Material and methods Five commercially available composite resins were studied. Nine disc-shaped specimens (6x2mm) were fabricated from each composite. The specimens were randomly allocated into three groups and three different treatments were performed on each group: storage in water (control group), water-jet flossing using 50 Psi water pressure, and water-jet flossing using 100 Psi water pressure. The water-jet flossing was performed in a standardized manner using a Waterpik® Aquarius® water flosser. Color and roug…
Effect of cavity preparation instruments (oscillating or rotating) on the composite-dentin interface in primary teeth.
2003
Abstract Objectives: To evaluate the effect of preparation of instruments on the interfacial integrity between cavity wall and composite restoration. Methods: Two class II slot preparations were done in 10 primary teeth either with SonicSys® or with a conventional bur. The cavities were filled using an adhesive system. One layer of a flowable composite and one layer of a condensable composite were applied. The specimens were analyzed by confocal laser scanning microscopy. Results: In the SonicSys® group the mean thickness of the hybrid layer was 6.12 (0.60) μm; in the control group it was 6.04 (0.63) μm. The difference was not statistically significant. Two fractures were observed in one to…
Effect of aluminum chloride hemostatic agent on microleakage of class V composite resin restorations bonded with all-in-one adhesive
2012
Objectives: Since hemostatic agents can induce changes on enamel and dentin surfaces and influence composite resin adhesion, the aim of the present study was to evaluate the effect of the aluminum chloride hemostatic agent on the gingival margin microleakage of class V (Cl V) composite resin restorations bonded with all-in-one adhesive. Study design: Cl V cavities were prepared on the buccal surfaces of 60 sound bovine permanent incisors. Gingival margins of the cavities were placed 1.5 mm apical to the cemento-enamel junction (CEJ). The teeth were randomly divided into two groups of 30. In group 1, the cavities were restored without the application of a hemostatic agent; in group 2, the ca…
Effect of framework type on survival probability of implant-supported temporary crowns : an in vitro study
2020
Made available in DSpace on 2020-12-12T01:29:18Z (GMT). No. of bitstreams: 0 Previous issue date: 2020-01-01 Background: This in vitro study evaluated the effect of framework type on the survival probability of temporary implant-supported crowns and on the implant platform structure after dynamic fatigue. Material and Methods: Thirty (30) external hexagon implants (3.75 x 10 mm) were embedded in acrylic resin following the ISO-14801. Standardized temporary crowns (n=10, N=30) were manufactured in acrylic resin and divided according to the framework type: Total plastic, Plastic with CoCr base and Titanium. The crowns were installed onto the implants (20N. cm) and fatigued (100N, 2 Hz) to det…
Water diffusion and swelling stresses in ionizing radiation cured epoxy matrices
2017
Abstract In this work a DGEBF epoxy monomer was cured by electron beam radiation in the presence of an iodonium salt and the obtained system was hydrothermally aged as such and also after a thermal treatment, in order to obtain two systems having different uniformity in the cross-linking degree. On both systems, the transient stress field arising from swelling was measured and monitored by an optical Photoelastic technique and the results were commented with reference to a thermally cured epoxy system containing the same monomer and already discussed in a previous work. Beam samples with identical dimensions, obtained from the irradiated systems, have been aged at 80 °C in water, and charac…
Effect of different bleaching protocols on whitening efficiency and enamel superficial microhardness
2018
Background Tooth bleaching is a popular aesthetic treatment to modify the color of teeth. Despite the extensive literature concerning the subject, there is still no consensus regarding the application mode of the different bleaching agents and their effect on enamel. Therefore, this study evaluated the influence of different bleaching protocols on whitening efficiency and enamel superficial hardness. Material and methods Bovine enamel fragments were embedded in acrylic resin and wet-sanded to obtain a flat buccal surface. The specimens were then randomly divided into 6 groups (n=10), based on the bleaching material [HP Maxx 35% (35% hydrogen peroxide), HP Blue 35% (35% hydrogen peroxide + C…
Water diffusion and swelling stresses in highly crosslinked epoxy matrices
2016
Abstract The present work investigates the swelling induced stresses arising in two epoxy systems during water uptake. The analysed systems are two epoxy resin based on DGEBA monomer and DGEBF monomer respectively, both fully cured by DDS amine. The systems achieve different cross-link density degrees, and are characterised by high glass transition temperatures ranging between 200 and 230 °C. Both epoxies have been conditioned in deionized water baths at two different temperatures (50 °C and 80 °C). A desorption process at room temperature in a dry airborne environment was performed after saturation. Dynamic Mechanical Thermal Analysis, carried out at the various stages of hydrothermal cond…
Simultaneous measurement of temperature and strain in glass fiber/epoxy composites by embedded fiber optic sensors: I. Cure monitoring
2007
In this paper (Part I) the use of fiber optic sensors for real-time monitoring of the cure kinetics of GFRP composites is explored. The proposed sensing system allows the simultaneous measurement of both temperature and strain by monitoring the change in reflected wavelength from two coupled fiber Bragg grating (FBG) sensors that have been embedded into the composite laminate. Instrumented GFRP laminates with 12, 18 and 24 reinforcing plies, respectively, were prepared by means of the vacuum bagging technique. Samples were cured in a thermally controlled oven at 80 degrees C and 30 kPa for 240 min (isothermal stage) and then cooled down to ambient temperature by turning off the heating sour…
Combining magnetic field induced locomotion and supramolecular interaction to micromanipulate glass fibers: toward assembly of complex structures at …
2011
The formation of ordered complex structures is one of the most challenging fields in the research of biomimic materials because those structures are promising with respect to improving the physical and mechanical properties of man-made materials. In this letter, we have developed a novel approach to fabricating complex structures on the mesoscale by combining magnetic-field-induced locomotion and supramolecular-interaction-assisted immobilization. We have employed a magnetic field to locomote the glass fiber, which was modified by the layer-by-layer self-assembly of magnetic nanoparticles, to desired positions and have exploited the supramolecular interaction to immobilize glass fiber onto …