The formal redox potential of the Yb(III,II) Couple at 0°C in 3.22 molal NaCl medium
2004
Following our previous investigations on aqueous solutions of hypooxidized and iperoxidized species, we managed, by lowering the temperature of the solutions to 0 degrees C, to obtain, by electrochemical methods, Yb(II) and Yb(III) mixtures, enough stable to determine by a potentiometric method the formal redox potential of the Yb(IlI, II) couple. Its value, in a large range of total Ytterbium concentration, is -1233 +/- 3 mV against the molal hydrogen electrode in the 3.22 m NaCl medium.
Synthesis of Yb nanoparticles by laser ablation of ytterbium target in sodium bis(2-ethylhexyl)sulfosuccinate reverse micellar solution
2010
Abstract Surfactant-coated ytterbium nanoparticles were produced by Nd:YAG laser ablation of a Yb bulk target immersed in sodium bis(2-ethylhexyl)sulfosuccinate (AOT)/ n -heptane micellar solution. In our experimental conditions, as highlighted by IR spectroscopy, AOT molecules are not decomposed by the intense laser pulses but play a pivotal role in the stabilisation of Yb nanoparticles. The formation of Yb nanoparticles in the liquid phase was monitored by UV–Vis spectroscopy whereas the Yb/AOT composites obtained by evaporation of the organic solvent were characterised by XPS and TEM. Data analysis consistently shows the presence of surfactant-coated, nearly spherical and non-interacting…
High-resolution characterization of the diffusion of light chemical elements in metallic components by scanning microwave microscopy
2014
International audience; An original sub-surface, high spatial resolution tomographic technique based on scanning microwave microscopy (SMM) is used to visualize in-depth materials with different chemical compositions. A significant phase difference in SMM between aluminum and chromium buried patterns has been observed. Moreover this technique was used to characterize a solid solution of a light chemical element (oxygen) in a metal lattice (zirconium). The large solubility of the oxygen in zirconium leads to modifications of the properties of the solid solution that can be measured by the phase shift signal in the SMM technique. The signal obtained in cross-section of an oxidized Zr sample s…
Study on the initial stages of water corrosion of fluorozirconate glasses
2004
Abstract The surface corrosion process associated with the hydrolysis of fluorozirconate glass, ZBLAN (53ZrF 4 , 20BaF 2 , 20NaF, 4LaF 2 , 3AlF 3 ) was investigated using X-ray photoelectron spectroscopy (XPS), grazing-incidence small angle X-ray scattering (GISAXS), X-ray reflectivity (XRR) and scanning electron microscopy (SEM). After a short exposure period (25 min) of the glass surface to deionized water the XPS data indicate an increase of the oxygen content accompanied by a decrease of fluorine concentration. The analysis of the chemical bonding structure identified the predominant surface reaction products as zirconium hydroxyfluoride and oxyfluoride species. The second most abundant…
Ethylene polymerization with FI complexes having novel phenoxy-imine ligands: Effect of metal type and complex immobilization
2011
A series of bis(phenoxy-imine) vanadium and zirconium complexes with different types of R3 substituents at the nitrogen atom, where R3 = phenyl, naphthyl, or anthryl, was synthesized and investigated in ethylene polymerization. Moreover, the catalytic performance was verified for three supported catalysts, which had been obtained by immobilization of bis[N-(salicylidene)-1-naphthylaminato]M(IV) dichloride complexes (M = V, Zr, or Ti) on the magnesium carrier MgCl2(THF)2/Et2AlCl. Catalytic performance of both supported and homogeneous catalysts was verified in conjunction with methylaluminoxane (MAO) or with alkylaluminium compounds (EtnAlCl3−n, n = 1–3). The activity of FI vanadium and zirc…
V-containing ZrO2 inorganic yellow nano-pigments
2015
In this work we report new results on the preparation, characterization and color properties of the inorganic yellow nano-pigmenting system based on monoclinic V–ZrO2 solid solution nanoparticles. The series of solid solution nanopowders were obtained by a polyol technique where the precipitates, obtained after heating at 180 °C ethylene glycol solutions of vanadyl acetonate and zirconium n-propoxide, were annealed at different temperatures up to 1300 °C for a short duration, in order to improve their crystallinity and control the crystalline form of the final nanoparticles. On annealing at around 450 °C highly crystalline tetragonal V-containing zirconia particles were developed, which tra…
Microstructure of Fe–ZrSiO4 solid solutions prepared from gels
2012
Abstract Microstructural changes associated with chemical and structural evolution from gels to Fe x –ZrSiO 4 solid solutions are reported. Mineralizer-free Fe x –ZrSiO 4 gels in the compositional range 0 ≤ x ≤ 0.15 were prepared by sol–gel liquid-phase route from mixtures of alkoxides of silicon and zirconium, and iron (III) acetylacetonate, and annealed at different temperatures and/or times. The first step on the whole process to the final Fe x –ZrSiO 4 solid solutions was the formation of aggregated of tetragonal Fe-doped ZrO 2 nanocrystals with diameters smaller than 50 nm. At this stage the tetragonal Fe–ZrO 2 were embedded in amorphous silica resulting nanocomposite materials. The …
Microstructural Evolution from Praseodymium-Containing Zircon Gels to Prx-ZrSiO4 Solid Solutions
2012
Structural evolution and coupled microstructural transformations occurred on annealing mineralizer-free Pr-containing ZrSiO4 gels up to final praseodymium-doped zircon yellow pigments are reported. Gels with nominal compositions Prx-ZrSiO4, 0 ≤ x ≤ 0.125, were prepared from mixtures of zirconium and silicon alkoxides and praseodymium acetylacetonate. Crystallization pathway and microstructural changes of thermally treated dried gels were followed by infrared spectroscopy, X-ray diffraction, field emission scanning and transmission electron microscopies, respectively. Results indicated that the crystallization pathway through the whole process of final Prx-ZrSiO4 solid solutions formation di…
Synthesis and characterization of praseodymium-containing ZrSiO4 solid solutions from gels
2011
Abstract The preparation and characterization of a series of praseodymium–zircon solid solution (Prx–ZrSiO4) materials with increasing nominal amounts of Pr is reported. Pr-doped zircon gels were prepared by gelling mixtures of zirconium n-propoxide, praseodymium acetylacetonate and tetraethylorthosilicate, and annealed over the range of temperature up to the formation of Pr–zircon solid solutions. The reaction sequence was followed by X-ray powder diffraction (XRD), ultraviolet–visible diffuse reflectance (DR) and infrared spectroscopy (IR). The first crystalline phase detected on annealing gels was a tetragonal praseodymium-containing ZrO2 phase (t-Pr–ZrO2). On further annealing, the subs…
The stoichiometry of blue vanadium doped zircon obtained by sol-gel methods
1992
Abstract In this study, Sol-Gel processes in aqueous solution were used to investigate the stoichiometry of the V/1bZrSiO 4 solid solutions achieved by this method. Compositions with a formal stoichiometric defect in: (a) ZrO 2 ([ZrO 2 ] 1−2x [SiO 2 ] [V 2 O 5 ] x ), and (b) in SiO 2 ([ZrO 2 ] [SiO 2 ] 1−2x [V 2 O 5 ] x ), x=0.02, 0.04, 0.05 and 0.10 have been prepared. X Ray Diffraction analyses in fired samples (1200°/3 days) showed that cristobalite and monoclinic zirconia appear as residual crystalline phase in (a) and (b) compositions respectively, except in sample (a) with x=0.02 in which no residual phase was detected and therefore is considered stoichiometric. This sample and sample…