Comparing the luminescence processes of YVO4:Eu and core-shell YVO4@YF3 nanocrystals with bulk-YVO4:Eu
Abstract Comparative analysis of bulk, non-coated and core-shelled nanocrystalline YVO4:Eu was performed by means of time-resolved luminescence and VUV excitation luminescence spectroscopy techniques. Nanocrystalline YVO4:Eu samples – both as-prepared and YF3 core-shelled – have been synthesized by means of a microwave-assisted synthesis in ionic liquids, which allows to obtain 10–12 nm nanoparticles with high crystallinity. The results show noticeable differences between bulk and nanocrystalline YVO4:Eu in photoluminescence experimental data, which explains by influence of the nanocrystal surface. A YF3 core-shell layer around YVO4:Eu nanoparticles partially recovers the intensity of the E…
Luminescence and ultraviolet excitation spectroscopy of SrI2 and SrI2:Eu2+
Abstract We report measurements of luminescence and its ultraviolet excitation spectra in SrI2 and SrI2:Eu2+ at temperatures of 10 and 300 K. Attention is focused on determining the exciton energy and its temperature shift from features of the excitation spectra and limits placed by absorption spectroscopy on a 120 μm thin crystal, on observation of a broadened Eu emission band attributed to trace Eu associated with oxygen in nominally undoped crystals, and on adding observations concerning the 3.4 eV band at low temperature attributed by Pustovarov et al. to the self-trapped exciton.
Polar nanoregions in Pb(Mg1/3Nb2/3)O3 (PMN): insights from a supercell approach
Abstract We report construction of a model of polar nanoregions in the PMN relaxor ferroelectric based on first-principles lattice dynamics for chemically ordered supercells [S.A. Prosandeev et al., Phys. Rev. B 70, 134110 (2004)], combined with invariance under permutations and dipole-dipole interaction as a source supporting randomly oriented residual polarization. Representative analytical estimates of polar nanore-gion — supercell mapping reproduce both nonzero local and zero macroscopic polarization of the structure, as well as the temperature change of the supercell anisotropy at cooling and field cooling.
Emerging blue-UV luminescence in cerium doped YAG nanocrystals
Physica status solidi / Rapid research letters 10(6), 475 - 479(2016). doi:10.1002/pssr.201600041
Electronic excitations in ZnWO4 and ZnxNi1−x WO4 (x = 0.1 − 0.9) using VUV synchrotron radiation
The photoluminescence spectra and luminescence excitation spectra of pure microcrystalline and nano-sized ZnWO4 as well as the Zn x Ni1−x WO4 solid solutions were studied using vacuum ultraviolet (VUV) synchrotron radiation. The samples were also characterized by x-ray powder diffraction. We found that: (i) the shape of the photoluminescence band at 2.5 eV, being due to radiative electron transitions within the [WO6]6− anions, becomes modulated by the optical absorption of Ni2+ ions in the Zn x Ni1−x WO4 solid solutions; and (ii) no significant change in the excitation spectra of Zn0.9Ni0.1WO4 is observed compared to pure ZnWO4. At the same time, a shift of the excitonic bands to smaller en…
Comparative study of the luminescence properties of macro- and nanocrystalline MgO using synchrotron radiation
MgO nano-powder with an average crystallite size of nanoparticles ranging 10-15 nm was synthesized using the extractive-pyrolytic method and was studied by room temperature VUV spectroscopy under synchrotron radiation excitation. Comparative analysis of their luminescent properties with that of mac- rocrystalline powder analogues and an MgO single crystal, grown by the arc-fusion method, has been per- formed under excitation by pulsed VUV synchrotron radiation. Special attention was paid to VUV spectral range, which is not reachable with commonly used lamp and laser sources. A considerable blue shift of about 0.3 eV in the excitation spectra of 2.95 eV emission band, was revealed in nanocry…
Numerical Evidences of Polarization Switching in PMN Type Relaxor Ferroelectrics
We present a conceptual and computational framework for chemically ordered Pb(Mg 1/3 Nb 2/3 O 3) (PMN) type supercells violating disorder of the host lattice. The effective Hamiltonian is specified by invariance under permutations of supercells and by the dipole-dipole interaction supporting both local nonzero and zero mean polarization of the structure. Statistics treated in canonical ensemble within the mean field approach reveals emergence of polar nanoregions as supported by interplay between the (random) initial state polarization of supercells and their interactions increased at cooling.
X-RAY PHOTOEMISSION ELECTRON MICROSCOPE DETERMINATION OF ORIGINS OF ROOM TEMPERATURE FERROMAGNETISM AND PHOTOLUMINESCENCE IN HIGHCo-CONTENTCoxZn1-xOFILMS
In this paper, we reported on the X-ray photoemission electron microscope (XPEEM) determination of magnetic and luminescence origins for two CoxZn1-xO films. The cobalt fraction x of radio frequency co-sputtered samples were 0.86(2) and 0.92(2), respectively. Films were ferromagnetic and semiconductive. Unique narrow green color lines beside the ZnO intrinsic emissions were found with a decay time in microsecond range at room temperature. Origins of magnetic and luminescence properties were determined with XPEEM. The X-ray absorption near edge structure at the Co L3-edge denoted that Co was partially oxidized, and phase-contrast images together with chemical composition identification furt…
Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics
Abstract Optical and luminescence properties of transparent nanosized cerium doped Y 3 Al 5 O 12 (YAG:Ce) ceramics have been studied. YAG:Ce nanoceramics were obtained by means of low temperature and high pressure (LTHP) sintering method. Nanoceramic samples were sintered in the 2–8 GPa pressure range, whereas Ce 3+ concentration was varied in the 0.5–5 at. % range. It is shown that, in contrast to the single crystal, a strong rise of absorption coefficient was detected already at wavelength shorter than 400 nm in all nanoceramic samples studied. Furthermore, in nanoceramic samples unusual UV emission band near 3.1 eV was observed, which is not observed in the YAG:Ce single crystal. High pr…