Formation and Rupture of Schottky Nanocontacts on ZnO Nanocolumns
In this paper, the electrical transport and mechanical properties of Pt/ZnO Schottky nanocontacts have been studied simultaneously during the formation and rupture of the nanocontacts. By combining multidimensional conducting scanning force spectroscopy with appropriated data processing, the physical relevant parameters (the ideality factor, the Schottky barrier height, and the rupture voltage) are obtained. It has been found that the transport curves strongly depend on the loading force. For loading forces higher than a threshold value, the transport characteristics are similar to those of large-area Schottky contact, while below this threshold deviations from strictly thermionic emission …
Anisotropic chemical etching of semipolar \{10\bar {1}\bar {1}\}\mbox {/} \{10\bar {1}{+}1\} ZnO crystallographic planes: polarity versus dangling bonds
ZnO thin films grown by metal?organic vapor phase epitaxy along the nonpolar direction and exhibiting semipolar facets have been chemically etched with HCl. In order to get an insight into the influence of the ZnO wurtzite structure in the chemical reactivity of the material, Kelvin probe microscopy and convergent beam electron diffraction have been employed to unambiguously determine the absolute polarity of the facets, showing that facets are unstable upon etching in an HCl solution and transform into planes. In contrast, facets undergo homogeneous chemical etching perpendicular to the initial crystallographic plane. The observed etching behavior has been explained in terms of surface oxy…