Eugenio Cantelar
Dual-polarization-pump CW laser operation in Nd3+:LiNbO3 channel waveguides fabricated by reverse proton exchange
Abstract In this work, continuous-wave laser action at 1084.5 nm at room temperature in LiNbO 3 :Nd 3+ channel waveguides, fabricated by reverse proton exchange (RPE), is reported. The sample was pumped at λ = 808 nm in either σ or π-polarized configurations, TE- and TM-pumping schemes, being the laser emission π-polarized at all power levels. The laser characteristics, as function of the pumping scheme (TE or TM), have been obtained. In both cases, the laser emission was stable, without any reduction in the output power even under continuous pump operation at maximum power at room temperature, indicating high resistance to photorefractive damage.
Multi-line NIR-RGB emission in Nd:LiNbO3 RPE optical waveguides
Simultaneous generation of four spectral emission lines has been achieved in Nd-doped lithium niobate reverse proton exchange optical waveguide cavities. Using a pump at 800 nm, the four lines were found and they are due to lasing at 1.3735 combined with parametric conversion at 0.687, 0.574 and 0.4 mum.
Scanning near-field optical microscopy (SNOM) of lithium niobate aperiodically poled during growth
In the present work, aperiodically poled lithium niobate (APPLN) was grown, along the a-axis, by the off-centred Czochraski method. The domain formation has been triggered by rare earth doping, using in this case Er3+ and Yb3+ ions. The growth conditions were selected in order to obtain a modulated domain distribution. SNOM measurements have been performed with a Nanonics Imaging Ltd model MultiView 200 TM working in non-contact tapping mode.
Modelling of Laser Operation in RPE Nd3+:LiNbO3 Channel Waveguides
In this work, laser action in RPE Nd3+:LiNbO3 is modelled by using the overlapping integrals method. Different pumping schemes, TE or TM, have been considered in order to reproduce the experimental measurements. Calculated results indicate that the slope efficiency remains basically independent on the pumping scheme while the threshold pump power increases for TE pumping.
Near-field scanning optical microscopy to study nanometric structural details of LiNbO3 Zn-diffused channel waveguides
A near-field scanning optical microscope (NSOM) is used to perform structural and optical characterization of the surface layer after Zn diffusion in a channel waveguide fabricated on lithium niobate. A theoretical approach has been developed in order to extract refractive index contrast from NSOM optical transmission measurements (illumination configuration). As a result, different solid phases present on the sample surface can be identified, such as ZnO and ZnNb2O6. They appear like submicrometric crystallites aligned along the domain wall direction, whose origin can be ascribed to some strain relaxation mechanism during the annealing process after Zn diffusion. Jose.Canet-Ferrer@uv.es
SNOM study of ferroelectric domains in doped LiNbO3 crystals
Abstract This work shows a study of the periodic ferroelectric domains formed in LiNbO3 crystals doped with rare earths by means of scanning near field optical microscopy (SNOM) technique. It has been observed periodic structures associated with ferroelectric domains with an unexpected high value of the optical contrast working under reflectance SNOM mode. From Raman-Nath diffraction patterns, a refractive index modulation of Δ n ∼ 1 0 − 4 has been calculated. These results were correlated with the ferroelectric periodic domains obtained by the SNOM technique. A light waveguide effects along the ferroelectric domains is suggested to explain the high reflectance contrast observed in SNOM exp…