Ferromagnetic and paramagnetic magnetization of implanted GaN:Ho,Tb,Sm,Tm films
The SQUID magnetic measurements were performed on the GaN films prepared by metal-organic vapour phase epitaxy and implanted by Tb3+, Tm3+, Sm3+, and Ho3+ ions. The sapphire substrate was checked by the electron paramagnetic resonance method which showed a content of Cr3+ and Fe3+ impurities. The samples 5 × 5 mm2 were positioned in the classical straws and within an estimated accuracy of 10−6 emu, no ferromagnetic moment was detected in the temperature region of 2–300 K. The paramagnetic magnetization was studied for parallel and perpendicular orientation. In the case of GaN:Tb sample, at T = 2 K, a pronounced anisotropy with the easy axis perpendicular to the film was observed which can b…
Platinum-doped CeO2 thin film catalysts prepared by magnetron sputtering.
The interaction of Pt with CeO(2) layers was investigated by using photoelectron spectroscopy. The 30 nm thick Pt doped CeO(2) layers were deposited simultaneously by rf-magnetron sputtering on a Si(001) substrate, multiwall carbon nanotubes (CNTs) supported by a carbon diffusion layer of a polymer membrane fuel cell and on CNTs grown on the silicon wafer by the CVD technique. The synchrotron radiation X-ray photoelectron spectra showed the formation of cerium oxide with completely ionized Pt(2+,4+) species, and with the Pt(2+)/Pt(4+) ratio strongly dependent on the substrate. The TEM and XRD study showed the Pt(2+)/Pt(4+) ratio is dependent on the film structure.