Effect of Er3+-doping on 65GeS2-25Ga2S3-10CsCl glass probed by annihilating positrons

Abstract Effect of Er3+-doping resulting in pronounced mid-IR fluorescence functionality was examined first in chalcohalide 65GeS2-25Ga2S3-10CsCl glass using positron annihilation lifetime (PAL) spectroscopy. The detected PAL spectra were reconstructed from unconstrained x2-term analysis employing two-state simple trapping model for one kind of positron trapping free-volume defects, the parameterization being performed at the example of 65GeS2-25Ga2S3-10CsCl glass doped with 0.6 at. % of Er3+. The observed decrease in positron trapping rate was proved to be primary void-evolution process in this Er-activated glass, like in many other chalcogenide glasses affected by rare earth doping. The n…