0000000000722903
AUTHOR
Baharak Divband
Zeolite-silver-zinc nanoparticles : biocompatibility and their effect on the compressive strength of mineral trioxide aggregate
Background This study was carried out to evaluate the biocompatibility of zeolite-silver-zinc (Ze-Ag-Zn) nanoparticles and their effect on the compressive strength of Mineral Trioxide Aggregate (MTA). Material and Methods Biocompatibility was evaluated by an MTT assay on the pulmonary adenocarcinoma cells with 0.05, 0.1, 0.25, 0.5, 1 and 5 mg/mL concentrations of Ze-Ag-Zn. For compressive strength test, four groups containing 15 stainless-steel cylinders with an internal diameter of 4 and a height of 6 mm were prepared and MTA (groups 1 and 2) or MTA + 2% Ze-Ag-Zn (groups 3 and 4) were placed in the cylinders. The compressive strength was evaluated using a universal testing machine 4 days a…
The effect of photodynamic therapy and polymer solution containing nano-particles of Ag /ZnO on push-out bond strength of the sealers AH-Plus and MTA Fillapex
BACKGROUND The aim of this in vitrostudy was to examine and compare the effect of photodynamic therapy and solution containing nano particles Ag/ZnO on adhesion of endodontic sealers to dentinal walls of human root canal. MATERIAL AND METHODS Ninty single-rooted human teeth were selected and their clinical crown was cut from the cemento-enamel junction zone. Canals were prepared by RaCe rotary system and the smear layer was removed using 17% EDTA and 5.25% NaOCl. Samples were randomly divided into two groups of AH Plus and MTA Fillapex based on the sealer type and each group based on antimicrobial method was divided into two sub-groups of photodynamic therapy and polymer containing nano par…
Biocompatibility of Mineral Trioxide Aggregate with TiO2 Nanoparticles on Human Gingival Fibroblasts
Background The New compositions of white mineral trioxide aggregate (WMTA) or use of various additives like nanoparticles might affect MTA’s ideal characteristics This study was performed to evaluate the cytotoxicity of WMTA and WMTA with Titanium dioxide (TiO2) nanoparticles (1% weight ratio) at different storage times after mixing on human gingival fibroblasts (HGFs). Material and Methods HGFs were obtained from the attached gingiva of human premolars. HGFs were cultured in Dulbecco’s Modified Eagle medium, supplemented with 10% fetal calf serum, penicillin and streptomycin. The cells were exposed to WMTA (groups 1 and 2) and WMTA+TiO2 (groups 3 and 4). The fifth and sixth groups served a…
Effect of the TiO2 nanoparticles on the selected physical properties of mineral trioxide aggregate
Background Some of the efforts to improve the properties of Mineral Trioxide Aggregate (MTA) include incorporation of some nanoparticles such as Titanium dioxide (TiO2). The aim of this study was to evaluate the effect of TiO2 nanoparticles on the setting time, working time, push-out bond strength and compressive strength of MTA. Material and methods The physical properties to be evaluated were determined using the ISO 6786:2001 and 9917 specifications. Fifteen samples of each material (MTA or MTA with 1% weight ratio of TiO2 Nanoparticles) were prepared for any evaluated physical property. Data were analyzed using descriptive statistics and T-test. Statistical significance was set at P Res…