Zeolite-silver-zinc nanoparticles : biocompatibility and their effect on the compressive strength of mineral trioxide aggregate

subject

description

Background This study was carried out to evaluate the biocompatibility of zeolite-silver-zinc (Ze-Ag-Zn) nanoparticles and their effect on the compressive strength of Mineral Trioxide Aggregate (MTA). Material and Methods Biocompatibility was evaluated by an MTT assay on the pulmonary adenocarcinoma cells with 0.05, 0.1, 0.25, 0.5, 1 and 5 mg/mL concentrations of Ze-Ag-Zn. For compressive strength test, four groups containing 15 stainless-steel cylinders with an internal diameter of 4 and a height of 6 mm were prepared and MTA (groups 1 and 2) or MTA + 2% Ze-Ag-Zn (groups 3 and 4) were placed in the cylinders. The compressive strength was evaluated using a universal testing machine 4 days after mixing in groups 1 and 3, and 21 days after mixing in groups 2 and 4. Results There was no significant difference between cytotoxicity of different concentrations. The highest (52.22±18.92 MPa) and lowest (19.57±5.76 MPa) compressive strength were observed in MTA group after 21 days and in MTA + 2% Ze-Ag-Zn group after four days, respectively. The effect of time and 2% Ze-Ag-Zn on the compressive strength were significant (P<0.05). Mixing MTA with Ze-Ag-Zn significantly reduced and passage of time from day four to 21 significantly increased the compressive strength. Conclusions Mixing MTA with 2% Ze-Ag-Zn had an adverse effect on the compressive strength of MTA, but this combination had no cytotoxic effects. Key words:Compressive strength, Cytotoxicity, Mineral Trioxide Aggregate, Nanoparticle, Zeolite-Silver-Zinc.