Poly(N-isopropylacrylamide)-gated Fe3O4/SiO2 core shell nanoparticles with expanded mesoporous structures for the temperature triggered release of lysozyme

Core-shell nanoparticles comprised of Fe3O4 cores and a mesoporous silica shell with an average expanded pore size of 6.07 nm and coated with a poly(N-isopropylacrylamide) (PNIPAM) layer (CS MSNs EP PNIPAM) were prepared and characterized. The nanoparticles was loaded with (Ru(bipy)3 2+) dye or an antibacterial enzyme, lysozyme, to obtain CS MSNs EP PNIPAM Ru(bipy)3 2+ and CS MSNs EP PNIPAM Lys, respectively. The lysozyme loading was determined to be 160 mg/g of nanoparticle. It was seen that Ru(bipy)3 2+ and lysozyme release was minimal at a room temperature of 25 ºC while at physiological temperature (37 º C), abrupt release was observed. The applicability of the CS MSNs EP PNIPAM Lys was…