Nina E. Sweeney
Model-assisted ultrasonic calibration using intentionally embedded defects for in-process weld inspection
Abstract Automated in-process Non-Destructive Testing (NDT) systems are rapidly gaining traction within the manufacturing industry as they reduce manufacturing time and costs. When considering calibration and verification of such systems, creating defects of known geometry and nature during the deposition of a weld can: (I) help examine the capability of the automated system to detect and characterise defects, (II) be used to form a database of signals associated with different defect types to train intelligent defect classification algorithms, and (III) act as a basis for in-process gain calibration during weld inspection at high temperatures, where the ultrasound beam can be skewed as a r…
In-process calibration of a non-destructive testing system used for in-process inspection of multi-pass welding
Abstract In multi-pass welding, there is increasing motivation to move towards in-process defect detection to enable real-time repair; thus avoiding deposition of more layers over a defective weld pass. All defect detection techniques require a consistent and repeatable approach to calibration to ensure that measured defect sizing is accurate. Conventional approaches to calibration employ fixed test blocks with known defect sizes, however, this methodology can lead to incorrect sizing when considering complex geometries, materials with challenging microstructure, and the significant thermal gradients present in materials during the inter-pass inspection period. To circumvent these challenge…
Investigating the effect of residual stress on hydrogen cracking in multi-pass robotic welding through process compatible non-destructive testing
Abstract In this paper, the effect of Welding Residual Stress (WRS) on the size and morphology of hydrogen-induced cracks (HIC) is studied. Four samples were manufactured using a 6-axis welding robot and in two separate batches. The difference between the two batches was the clamping system used, which resulted in different amounts of welding deformation and WRS. The hydrogen cracks were intentionally manufactured in the samples using a localised water-quenching method, where water was sprayed over a specific weld pass in a predetermined position. The Phased-Array Ultrasonic Testing (PAUT) system was implemented during the welding process (high-temperature in-process method), to detect the …