Phase analysis and oxygen strorage capacity of ceria-lanthana-based TWC promoters prepared by sol-gel routes

subject

description

Ceria–lanthana-based promoters of three-way catalysts are synthesized by two different sol–gel routes, involving nitrate precursors. The oxygen uptake ability of these compounds is measured by O2 chemisorption. The specific surface area is determined by N2 adsorption (BET). X-ray diffraction data are analyzed by Rietveld refinement, demonstrating that lanthanum forms solid solution with CeO2; its total amount in ceria depends on the competitive formation of La–Al mixed oxides and on the synthetic method. The O2 uptake ability is essentially determined by the La content in the ceria–lanthana solid solution, while it is independent on the surface area and on the CeO2 particle size. The O2 uptake ability increases with the La:Ce relative amount in the ceria–lanthana solid solution, but decreases beyond a La:Ce molar ratio greater than ≃0.18. This behavior is ascribed to the stable association of vacancy–vacancy or vacancy dopant cation.