Pulsed laser growth and characterization of thin films on titanium substrates
2007
Abstract Colored layers were obtained by laser surface treatment of Ti substrates with a pulsed Nd:YAG Q-switched laser. The changes in the morphology, structure and chemical composition of the layers were studied by SEM, EDS, XPS, SIMS and Raman spectroscopy as a function of the laser fluence in the 4–60 J cm −2 . For laser fluences lower than 25 J cm −2 , the layers are colorless or yellow. Their surface is smooth, but they display cracks which increase when the fluence increases. The O/Ti ratio, determined by XPS analysis, varies from 0.7 (colorless layers) to 1.3 (yellow layer). Moreover, XPS spectra evidence non-negligible amounts of nitrogen and carbon in these layers. Raman spectra s…
Combined Adsorption/Photocatalytic dye removal by copper-titania-fly ash composite
2020
Abstract Achieving both photocatalytic efficiency and adsorption capacity is essential to produce a highly efficient photocatalyst. This study fabricated a new photocatalyst by combining copper (Cu) doped titanium dioxide (TiO2) with fly ash (FA). The photocatalysts were synthesized using mild acid (acid-FA/Cu/TiO2), base (base-FA/Cu/TiO2), and deionized water (rFA/Cu/TiO2) activated FA. EDX confirmed the inclusion of Cu in both Cu/TiO2 and FA/Cu/TiO2 composites. XRD analysis indicated the presence of the anatase form of TiO2 after Cu doping and incorporation into modified FA. All three FA/Cu/TiO2 composites demonstrated high absorption (UV and visible region) compared to their TiO2 and Cu/…
Nanostructured Pt–TiO2 composite thin films obtained by direct liquid injection metal organic chemical vapor deposition: Control of chemical state by…
2015
Abstract Nanostructured Pt–TiO 2 composite thin films were synthesized by direct liquid injection metal organic chemical vapor deposition process, using trimethyl(methylcyclopentadienyl)platinum and titanium isopropoxide as precursors. Surface and cross-sectional morphologies obtained by scanning electron microscopy and transmission electron microscopy evidenced the uniform distribution of platinum nanoparticles in the TiO 2 matrix. At higher Pt content, the X-ray diffraction analysis showed that the face-centered cubic phase of platinum appeared together with an anatase TiO 2 structure. In addition, as far as the platinum chemical state is concerned, the co-deposition of TiO 2 and Pt allow…
Thermal effects on the growth by metal organic chemical vapour deposition of TiO2 thin films on (100) GaAs substrates
2002
Abstract TiO 2 thin films were deposited on (100) GaAs substrates by LP-MOCVD with deposition temperatures ( T d ) ranking from 450 to 750 °C. The structure of these layers was studied by X-ray diffraction (XRD) and Raman spectroscopy. The growth of the TiO 2 anatase phase was observed for T d T d >600 °C. Finally, X-ray photoelectron spectrometry (XPS) and secondary ion mass spectroscopy (SIMS) experiments showed the presence of small quantities of Ga and As through the whole film thickness, slightly increasing at the surface of the layers. This result was related to the SEM observations and explained by considering the growth conditions.
Investigation on sol–gel synthesized Ag-doped TiO2 cermet thin films
2005
Abstract Undoped TiO 2 and Ag–TiO 2 (up to 23 at.% Ag) cermet thin films and polycrystalline powders have been prepared by sol–gel process. Their structure, composition, surface morphology and optical properties have been investigated by X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and ultraviolet–visible spectroscopy (UV–VIS spectroscopy). It has been observed that while Ag does not form a solid solution with TiO 2 , it promotes the anatase to rutile phase transformation. The transformation temperature decreases from 827 °C for undoped TiO 2 to about 650 °C fo…
TiO2 anatase films obtained by direct liquid injection atomic layer deposition at low temperature
2014
International audience; TiO2 thin films were grown by direct liquid injection atomic layer deposition (DLI-ALD) with infrared rapid thermal heating using titanium tetraisopropoxide and water as precursors. This titanium tetraisopropoxide/water process exhibited a growth rate of 0.018 nm/cycle in a self-limited ALD growth mode at 280 degrees C. Scanning electron microscopy and atomic force microscopy analyses have shown a smooth surface with a low roughness. XPS results demonstrated that the films were pure and close to the TiO2 stoichiometric composition in depth. Raman spectroscopy revealed that the films were crystallized to the anatase structure in the as-deposited state at low temperatu…
Study of the structural changes induced by air oxidation in Ti–Si–N hard coatings.
2008
International audience; 3-μm thick Ti–Si–N coatings were deposited on polished X38CrMoV5 substrates by sputtering a composite Ti–Si target in Ar–N2 reactive mixture. Oxidation tests were performed in air at 700 °C during 2 h. Whatever the silicon content in the range 0–4 at.%, no silicon containing compound was detected by XRD before air oxidation and only the TiN phase was evidenced. The mean grain size estimated from the full width at half maximum of the TiN (111) diffraction peak was close to 10 nm. As commonly reported for Ti–Si–N films, the hardness showed a maximum at 51 GPa versus the Si content. After oxidation of the TiN film, XRD and micro-Raman analyses revealed the occurrence of…
TiO2 nanostructures prepared by ferrocene/cobalt catalyst agents
2008
We present the growth and characterization of TiO2 nanocrystals. Nanostructured growth is obtained in a low-pressure CVD system by using an organometallic precursor Ti(OC3H7)4 as both the Ti and O source catalyzed by both ferrocene (an organometallic precursor) and cobalt metallic clusters prepared by the microwave-assisted polyol method. Two kinds of TiO2 structures were obtained in the cobalt clusters: a) pine-tree like (with short-leaf structure) and b) long-leaf structures as large as a few micrometers in size and both under 10 nm in thickness. Long-leaf TiO2 structures were grown at cobalt grain boundaries. For the growth conditions utilized, the TiO2 structures are composed of both an…
Highly stable defective TiO2-x with tuned exposed facets induced by fluorine: Impact of surface and bulk properties on selective UV/visible alcohol p…
2020
Abstract Titanium dioxide samples were prepared in the presence of different amounts of fluorine via hydrothermal method. It has been found that the presence of fluoride influenced the physico-chemical properties of TiO2 in various ways as polymorphic form stability, surface hydroxylation, generation of hydroxyl radicals under irradiation and formation of Ti3+ centers and oxygen vacancies. The generation rate of OH radicals was investigated by the photoluminescence technique in the presence of terephthalic acid. X-ray diffractometry indicated that fluorine stabilized the anatase TiO2. X-Ray photoelectron spectroscopy (XPS) revealed the presence of fluorine on the surface and the shift of th…
Photocatalytic thin films of TiO2 formed by a sol-gel process using titanium tetraisopropoxide as the precursor
2008
Abstract Thin TiO 2 films were prepared with the dip-coating technique by using sols deriving from titanium tetraisopropoxide. TiO 2 films were formed on glass substrates previously covered by a SiO 2 layer obtained from a tetraethylortosilicate sol. The films, after a thermal treatment at 673 K, mainly consisted of TiO 2 anatase. The samples were characterised by X-ray diffraction, UV–Vis spectroscopy, scanning electron microscopy and atomic force microscopy. The photoactivity of the various films was tested by using as probe reaction the photo-oxidation of 2-propanol in gas-solid regime. The photoreactivity results indicated that the TiO 2 films were efficient for degrading 2-propanol und…