Low-temperature luminescence of CdI2 under synchrotron radiation
2020
Synchrotron radiation is applied to study visible and UV luminescence spectra and their excitation spectra of undoped as well as In and Sb doped cadmium iodide crystals at 10 K. The origin of principal luminescence bands and the role of impurities in the formation of emission centers are discussed. The luminescence properties have been explained based on the electronic structure of CdI2 crystals.
Effect of Mn doping on the low-temperature synthesis of tricalcium phosphate (TCP) polymorphs
2019
Abstract Effect of Mn doping on the low-temperature synthesis of tricalcium phosphate (TCP) polymorphs was demonstrated in α- and β-TCP polymorphs prepared by wet precipitation method under identical conditions and annealed at 700 °C. Calcium phosphates with Mn doping level in the range from 1 to 5 mol% were studied and the formation of desired polymorph was controlled by varying Mn content in as-prepared precipitates. It was found that increasing Mn content resulted in the formation of β-TCP, while α-TCP was obtained with low Mn doping level, whereas a mixture of two polymorphs was obtained for intermediate Mn concentrations. Moreover, doping with Mn ions allowed the synthesis of β-TCP at …
X-ray and dielectric characterization of Co doped tetragonal BaTiO3 ceramics
2016
ABSTRACTThe crystal structure modifications of BaTiO3 induced by cobalt doping were studied. The polycrystalline (1 − x)BaTiO3 + xCo2O3 samples, with x ≤ 10 wt.%, were prepared by high temperature sintering conventional method. According to X-ray phase and structural characterization, performed by full-profile Rietveld refinement technique, all synthesized samples showed tetragonal symmetry perovskite structure with minor amount of parasitic phases. Pure single-phase composition has been detected only in the low level of doping BaTiO3. It was indicated that substitution of Co for the Ti sites in the (1 − x)BaTiO3 + xCo2O3 series led to decrease of tetragonality (c/a) of the BaTiO3 perovskit…
Reduced temperature sensitivity of multicrystalline silicon solar cells with low ingot resistivity
2016
This study presents experimental data on the reduction of temperature sensitivity of multicrystalline silicon solar cells made from low resistivity ingot. The temperature coefficients of solar cells produced from different ingot resistivities are compared, and the advantages of increasing the net doping are explained.
Reducing the Schottky barrier height at the MoSe2/Mo(110) interface in thin-film solar cells: Insights from first-principles calculations
2016
Abstract We report on first-principles calculations of the properties of the MoSe2/Mo(110) interface. Due to mismatch between the lattice parameters of the two structures, different patterns can form at the interface. We have studied the formation energy and the band alignment of six patterns for the MoSe2 (0001)/Mo(110) interface and one pattern for the MoSe2 (11 2 0)/Mo(110) interface. The MoSe2 (11 2 0)/Mo(110) interface is more stable than the MoSe 2 (0001)/Mo(110) interface and in contrast to MoSe2 (0001)/Mo(110), no Schottky barrier forms at MoSe2 (11 2 0)/Mo(110). Doping with Na modifies the band alignment at the interfaces. The Schottky barrier height decreases, provided that a Na a…
Emerging blue-UV luminescence in cerium doped YAG nanocrystals
2016
Physica status solidi / Rapid research letters 10(6), 475 - 479(2016). doi:10.1002/pssr.201600041
Shallow and deep trap levels in X-ray irradiated β-Ga2O3: Mg
2019
Abstract The results of the investigation of thermostimulated luminescence (TSL) and photoconductivity (PC) of the X-ray irradiated undoped and Mg2+ doped β-Ga2O3 single crystals are presented. Three low-temperature peaks at 116 K, 147 K and 165 K are observed on the TSL glow curves of undoped crystals. The high-temperature TSL peaks at 354 K and 385 K are dominant in Mg2+ doped crystals. The correlation between doping with Mg2+ ions and the local energy levels of the intrinsic structural defects of β-Ga2O3, which are responsible for the TSL peaks and PC, is established. The nature of TSL peaks and the appropriate photoconductivity excitation bands are discussed.
Influence of Sr addition on structural, dielectric and Raman properties of Na0.5Bi0.5TiO3ceramics
2016
ABSTRACTLead free (Na0.5Bi0.5)1-xSrxTiO3 (x = 0, 0.01 and 0.02) ceramics were produced by a conventional solid-state sintering method. X-ray diffraction analysis shows that the obtained samples possess the perovskite structure with rhombohedral symmetry. The microstructure study shows a dense structure, in agreement with the relative density (above 97%). Dielectric analysis revealed the diffuse character of the electric permittivity anomalies and their shift to a lower temperature range after Sr doping of NBT. The Raman spectra are similar for all samples in agreement with the X-ray diffraction data. The possible origin of the observed effects was discussed.
Dielectric, thermal and Raman spectroscopy studies of lead-free (Na0.5Bi0.5)1−xSrxTiO3 (x = 0, 0.04 and 0.06) ceramics
2016
ABSTRACTLead-free (Na0.5Bi0.5)1−xSrxTiO3 (x = 0, 0.04 and 0.06) ceramics with relative densities above 97% were prepared by solid-state synthesis process. Their dielectric, thermal and Raman properties were studied. X-ray diffraction analysis shows perovskite structure with rhombohedral symmetry at room temperature. Sr doping of Na0.5Bi0.5TiO3 (NBT) results in an increase of the dielectric permittivity, diffusing of the permittivity maximum and its shift toward lower temperatures. The temperature of the rhombohedral–tetragonal phase transition indicated by the differential scanning calorimetry (DSC) peak and relaxational dielectric anomaly near the depolarization temperature are also shifte…
Non-Linearity Extremum in Niobium Doped Potassium Tantalate
1997
We report non-linear dielectric measurements in the KTaO 3 :Nb system (x Nb ≤ 0.05). The non-linear susceptibility diverges at low temperatures and reaches maximum values in the intermediate range (0.0075 ≤ x Nb ≤ 0.02). To account for this extremum non linearity, we propose a model of temperature dependent clusters which fits with a number of experimental reports. We also suggest that this model may be applied to the related compounds SrTiO 3 :Ca and KTaO 3 :Na.