Crystal structure and physical properties of Mg6Cu16Si7-type M6Ni16Si7, for M=Mg, Sc, Ti, Nb, and Ta
2008
Five compounds were investigated for magnetic character and superconductivity, all with non-magnetic nickel and band structures containing flat bands and steep bands. The syntheses and crystal structures, refined by powder X-ray diffraction, are reported for M{sub 6}Ni{sub 16}Si{sub 7}, where M = Mg, Sc, Ti, Nb, and Ta. All compounds form in the Mg{sub 6}Cu{sub 16}Si{sub 7} structure type. Resistance measurements are also reported on M{sub 6}Ni{sub 16}Si{sub 7} (M = Mg, Sc, Ti, and Nb) down to 0.3 K, with all four showing metallic conductivity. No superconductivity is observed. Magnetization measurements for all compounds reveal essentially temperature independent paramagnetism, with a tend…
Preparation and properties of Tl2Ba2CaCu2O8 thin films
1994
Anex situ process has been developed to produce thin superconducting Tl2Ba2CaCu2O8 films. The properties of films grown on different substrates using different annealing regimes were studied. Critical temperatures of 103–107 K were measured on films prepared in a broad range of annealing temperatures on SrTiO3, LaAlO3, and Y-ZrO2 substrates. A critical current density,Jc, of 2×106 A/cm2 at 77 K was measured on LaAlO3. Film morphology was studied by SEM, AFM, and STM.
Complete stabilization and improvement of the characteristics of tunnel junctions by thermal annealing
2006
We have observed that submicron sized Al--AlO{$_x$}--Al tunnel junctions can be stabilized completely by annealing them in vacuum at temperatures between $350^{\circ}$C and $450^{\circ}$C. In addition, low temperature characterization of the samples after the annealing treatment showed a marked improvement of the tunneling characteristics due to disappearance of unwanted resonances in the current. Charging energy, tunneling resistance, barrier thickness and height all increase after the treatment. The superconducting gap is not affected, but supercurrent is reduced in accordance with the increase of tunneling resistance.
Growth characteristics of sputter-deposited thin films
1996
Thin films of the heavy-fermion superconductor were deposited on various substrate materials in various orientations by means of a quasi-multilayer sputter process. Strongly (0001)-textured growth of the hexagonal compound was found for a uranium content in the range of 23% to 28% on sapphire and with perfect in-plane order on the latter substrate material. Atomic force microscopy and scanning electron microscopy revealed a Vollmer - Weber-like growth mode resulting in the development of large compressive strain in films on . As a result the electronic transport properties - in particular the temperature dependence of the resistivity - were strongly renormalized. Strong deviations from the …
Superconductivity in high‐quality (Hg 0.9 Re 0.1 )Ba 2 CaCu 2 O 6+ δ HTSC thin films
2004
High-quality epitaxial (Hg0.9Re0.1)Ba2CaCu2O6+δ (HgRe-1212) HTS thin films were successfully prepared using pulsed laser deposition (PLD) of the Re0.1Ba2CaCu2O6+δ precursor and subsequent Hg vapor annealing. The thin films exhibit a sharp superconducting transition at Tc ≈ 120 K. The resistive transitions have been investigated in magnetic fields up to 6 T parallel and perpendicular to the c-axis. We have determined the activation energy of thermally activated flux-motion for both magnetic field orientations. (© 2004 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)
Experimental research regarding the study of surface quality of aluminum alloys processed through milling
2017
The aim of this paper is to present the necessary steps to conduct a design of experiment with application on the aluminum alloy surface quality obtained by end-milling process. The machined surface quality is influenced by the cutting process parameters, and especially by their variation. The research methods used in this paper are the Taguchi method - to determine the cutting parameters influence, on the surface quality, and the full factorial design of experiment to confirm the results obtained by Taguchi’s method and to determine the percentage of the parameters influence involved in the process.
Study of the cutting process parameters that influence the surface quality machined by end milling of the aluminum alloy
2019
This research aims to carry out an elaborate experiment by witch resulting in relevant conclusions that have practical applicability in the aeronautical industry. The surface roughness measured transversely and longitudinally on the feed motion direction of the cutting tool constitutes the dedicated objective function on which the study was conducted in this case. The end milling was chosen of an aluminum alloy used explicitly in the aeronautical industry. The actual experiments were carried out in the only aeronautical industry in Romania carrying out these types of machining and were made according to the methodology with rigorous experimental planning of the research. The experimental pl…
High Temperature Corrosion Behaviour of Coated F17Ti Stainless Steel
1997
Nous avons etudie l'effet de revetements de chromine et d'alumine sur le comportement de l'acier inoxydable F17Ti. Les films ont ete formes a la surface de l'alliage par pyrolyse de la vapeur d'un precurseur organometallique (MOCVD). Cette technique permet egalement de preparer des oxydes d'elements de terres rares. Ceci nous a conduit a envisager la formation de couches barrieres dopees par un element actif, soit par depots successifs, soit par codeposition de chromine ou d'alumine et d'un oxyde de terre rare, suivi d'un traitement de recuit d'homogeneisation. Les revetements ainsi obtenus ont ete caracterises par microscopie electronique a balayage, microanalyse X, diffraction des rayons …
Epitaxial growth of molybdenum on TiO2(110)
2003
Abstract Molybdenum was deposited on blue (i.e. non-stoichiometric) TiO2(1 1 0) surface using a very low deposition rate (less than 0.05 eqML min−1). The resulting deposit was investigated by means of X-ray photoelectron diffraction (XPD), LEED and XPS. Just after deposition, the film is mainly constituted of metallic molybdenum, contains oxygen homogeneously dispersed through the whole deposit and the broad features detected in XPD scans are interpreted as a coarse epitaxy between TiO2(1 1 0) surface and the (0 0 1) face of bcc molybdenum. The orientation relationship is: Mo(1 0 0)[0 0 1]//TiO2(1 1 0)[0 0 1]. After annealing the deposit at 673 K, XPD scans become sharper and epitaxy is ach…
AES and CEMS analysis of the formation of layers on Si steel under thermal treatment in a flux of H2/water vapour
1991
The near surface diffusion and reaction processes in iron-silicon steel (3.1 wt.%Si) during 10 min decarburization in water vapour/hydrogen have been studied. The decarburization temperature has been varied between 506 and 714°C for the fixed partial pressure ratio pH2O/pH2=0.017. An outer layer of SiO2 forms on the surface with its thickness increasing with temperature. From 600°C upwards, the decarburization process is hindered and a cementite layer is formed below the SiO2 layer. The formation of fayalite at the surface has been studied at a fixed decarburization temperature with pH2O/pH2 ranging from 0.017 to 0.49. The scale thickness reduces abruptly just before the ratio pH2O/pH2 nece…