Electronic and magnetic properties of Mn 12 molecular magnets on sulfonate and carboxylic acid prefunctionalized gold surfaces
2012
Structural, electronic, and magnetic properties of [Mn 12O 12(bet) 16(EtOH) 4](PF 6) 14·4CH 3CN·H 2O (in short Mn 12bet, bet = betaine = +N(CH 3) 3-CH 2-COO -) single-molecule magnets (SMMs) deposited on previously functionalized gold surfaces have been investigated. Self-assembled monolayers (SAMs) either of sodium mercaptoethanesulfonate (MES) or mercaptopropionic acid (MPA) are used as functionalization to avoid the direct interaction between the Mn 12bet molecules and the Au surface with the aim of preserving the main functional properties of the molecules. Scanning tunneling microscopy (STM) and X-ray photoemission spectroscopy (XPS) analysis show deposited Mn 12bet SMMs well-isolated …
Study of the structural phase transformation of iron oxide nanoparticles from an Fe2+ ion source by precipitation under various synthesis parameters …
2015
Abstract Magnetite nanoparticles were precipitated from a pure aqueous ferrous salt solution in an air atmosphere. The influence of the solution molarity, the rate of precipitator agent addition, stirring time and annealing temperature was studied. The morphology, crystalline phase purity and magnetic properties of the obtained powders were studied by X-Ray powder diffraction (XRD), Scanning electron microscopy (SEM), Differential thermal analysis (DTA), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XAS) and Vibrating sample magnetometer (VSM). The synthesis conditions were seen to have an effect on phase composition. It was possible to obtain near stoichiometric Fe…
Co doped ZnO nanowires as visible light photocatalysts
2016
Abstract High aspect ratio cobalt doped ZnO nanowires showing strong photocatalytic activity and moderate ferromagnetic behaviour were successfully synthesized using a solvothermal method and characterized by scanning electron microscopy (SEM), X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XAS), vibrating sample magnetometry (VSM) and UV–visible absorption spectroscopy. The photocatalytic activities evaluated for visible light driven degradation of an aqueous methylene orange (MO) solution were higher than for Co doped ZnO nanoparticles at the same doping level and synthesized by the same synthesis route. The rate constant for MO visi…
A new tool for nanoscale X-ray absorption spectroscopy and element-specific SNOM microscopy.
2007
Abstract Investigations of complex nanostructured materials used in modern technologies require special experimental techniques able to provide information on the structure and electronic properties of materials with a spatial resolution down to the nanometer scale. We tried to address these needs through the combination of X-ray absorption spectroscopy (XAS) using synchrotron radiation microbeams with scanning near-field optical microscopy (SNOM) detection of the X-ray excited optical luminescence (XEOL) signal. The first results obtained with the prototype instrumentation installed at the European Synchrotron Radiation Facility (Grenoble, France) are presented. They illustrate the possibi…
Chemical microimaging and microspectroscopy of surfaces with a photoemission microscope
1997
We applied element sensitive photoemission electron microscopy (PEEM) to investigate surfaces of devices built from complex materials. Conventional PEEM suffers from lack of information about the chemical composition of the imaged surface. Such information can be obtained by PEEM via tuning the photon energy to X-ray absorption edges. To apply spectromicroscopy we acquired and subtracted microscopic images using photon energies just below and at the edges. The resulting difference gives a micro-image of the lateral distribution of a specific element. Microspectroscopy is performed by recording the intensity of secondary electrons in selected spots during a sweep of the photon energy. We app…
The lateral variation of solid state reactions at surfaces studied by means of photoemission electron microscopy: formation of titanium silicides
2001
The alloying and oxygen reduction at titanium silicon interfaces were studied by means of photoemission microscopy. The microscopic chemical composition of the sample surface was characterised by means of imaging X-ray absorption. The silicide formation was studied at clean and oxidised silicon substrates both covered with micron-sized titanium patterns.
Investigation of phthalocyanine crystals exposed to NO2 ambient gas
2002
Crystals of free base phthalocyanine (H2pc) and its unsubstituted metal derivatives Mpc (where M=Ni, Cu, Zn, Pb, and pc=C32H16N8 2−=phthalocyanine ligand) were examined after being exposed to NO2 ambient gas. Scanning electron microscopy (SEM) supported by X-ray microprobe analysis (EDAX), UV–Vis and FTIR spectroscopy as well as X-ray powder diffractometry (XRD) were applied to study the crystals chemistry and surface morphology. The NO2 molecules were found to penetrate the crystal unit which led to the breakdown of the phthalocyanine macrocycle. The surface of the doped crystals has been scaled and covered by a layer composed predominantly of phthalimide. Despite vacuum desorption, it has…
Microscopic defects and impurity analyses of multicrystalline silicon solar cells from different manufacturing routes
2013
It is important to fully understand the physical behavior of solar cells made by materials from alternative process routes. Solar cells from Elkem Solar Grade Silicon and standard polysilicon have been investigated with light beam induced current and electroluminescence imaging. The low efficiency regions have been further analyzed by Scanning Electron Microscopy under different imaging modes. It was found that cell regions of low performance had undergone plastic deformations resulting in the creation of crystalline defects appearing as subgrain patterns. Similar patterns were observed in both ESS™ and standard polysilicon. Energy-dispersive X-ray spectroscopy (EDS) and electron backscatte…
Quantitative molecular plating of large-area 242Pu targets with improved layer properties
2015
Abstract For measurements of the neutron-induced fission cross section of 242Pu, large-area (42 cm2) 242Pu targets were prepared on Ti-coated Si wafers by means of constant current density molecular plating. Radiochemical separations were performed prior to the platings. Quantitative deposition yields (>95%) were determined for all targets by means of alpha-particle spectroscopy. Layer densities in the range of 100–150 μg/cm2 were obtained. The homogeneity of the targets was studied by radiographic imaging. A comparative study between the quality of the layers produced on the Ti-coated Si wafers and the quality of layers grown on normal Ti foils was carried out by applying scanning electron…
Mechanical characterization of TiO2 nanofibers produced by different electrospinning techniques
2015
Abstract In this work TiO2 nanofibers produced by needle and needleless electrospinning processes from the same precursor were characterized and compared using Raman spectroscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and in situ SEM nanomechanical testing. Phase composition, morphology, Young's modulus and bending strength values were found. Weibull statistics was used to evaluate and compare uniformity of mechanical properties of nanofibers produced by two different methods. It is shown that both methods yield nanofibers with very similar properties.