Thermal effects on the growth by metal organic chemical vapour deposition of TiO2 thin films on (100) GaAs substrates
2002
Abstract TiO 2 thin films were deposited on (100) GaAs substrates by LP-MOCVD with deposition temperatures ( T d ) ranking from 450 to 750 °C. The structure of these layers was studied by X-ray diffraction (XRD) and Raman spectroscopy. The growth of the TiO 2 anatase phase was observed for T d T d >600 °C. Finally, X-ray photoelectron spectrometry (XPS) and secondary ion mass spectroscopy (SIMS) experiments showed the presence of small quantities of Ga and As through the whole film thickness, slightly increasing at the surface of the layers. This result was related to the SEM observations and explained by considering the growth conditions.
Investigation on sol–gel synthesized Ag-doped TiO2 cermet thin films
2005
Abstract Undoped TiO 2 and Ag–TiO 2 (up to 23 at.% Ag) cermet thin films and polycrystalline powders have been prepared by sol–gel process. Their structure, composition, surface morphology and optical properties have been investigated by X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and ultraviolet–visible spectroscopy (UV–VIS spectroscopy). It has been observed that while Ag does not form a solid solution with TiO 2 , it promotes the anatase to rutile phase transformation. The transformation temperature decreases from 827 °C for undoped TiO 2 to about 650 °C fo…
TiO2 anatase films obtained by direct liquid injection atomic layer deposition at low temperature
2014
International audience; TiO2 thin films were grown by direct liquid injection atomic layer deposition (DLI-ALD) with infrared rapid thermal heating using titanium tetraisopropoxide and water as precursors. This titanium tetraisopropoxide/water process exhibited a growth rate of 0.018 nm/cycle in a self-limited ALD growth mode at 280 degrees C. Scanning electron microscopy and atomic force microscopy analyses have shown a smooth surface with a low roughness. XPS results demonstrated that the films were pure and close to the TiO2 stoichiometric composition in depth. Raman spectroscopy revealed that the films were crystallized to the anatase structure in the as-deposited state at low temperatu…
Study of the structural changes induced by air oxidation in Ti–Si–N hard coatings.
2008
International audience; 3-μm thick Ti–Si–N coatings were deposited on polished X38CrMoV5 substrates by sputtering a composite Ti–Si target in Ar–N2 reactive mixture. Oxidation tests were performed in air at 700 °C during 2 h. Whatever the silicon content in the range 0–4 at.%, no silicon containing compound was detected by XRD before air oxidation and only the TiN phase was evidenced. The mean grain size estimated from the full width at half maximum of the TiN (111) diffraction peak was close to 10 nm. As commonly reported for Ti–Si–N films, the hardness showed a maximum at 51 GPa versus the Si content. After oxidation of the TiN film, XRD and micro-Raman analyses revealed the occurrence of…
Removal of Surface Oxygen Vacancies Increases Conductance Through TiO(2) Thin Films for Perovskite Solar Cells
2019
[Image: see text] We report that UV–ozone treatment of TiO(2) anatase thin films is an efficient method to increase the conductance through the film by more than 2 orders of magnitude. The increase in conductance is quantified via conductive scanning force microscopy on freshly annealed and UV–ozone-treated TiO(2) anatase thin films on fluorine-doped tin oxide substrates. The increased conductance of TiO(2) anatase thin films results in a 2% increase of the average power conversion efficiency (PCE) of methylammonium lead iodide-based perovskite solar cells. PCE values up to 19.5% for mesoporous solar cells are realized. The additional UV–ozone treatment results in a reduced number of oxygen…
TiO2 nanostructures prepared by ferrocene/cobalt catalyst agents
2008
We present the growth and characterization of TiO2 nanocrystals. Nanostructured growth is obtained in a low-pressure CVD system by using an organometallic precursor Ti(OC3H7)4 as both the Ti and O source catalyzed by both ferrocene (an organometallic precursor) and cobalt metallic clusters prepared by the microwave-assisted polyol method. Two kinds of TiO2 structures were obtained in the cobalt clusters: a) pine-tree like (with short-leaf structure) and b) long-leaf structures as large as a few micrometers in size and both under 10 nm in thickness. Long-leaf TiO2 structures were grown at cobalt grain boundaries. For the growth conditions utilized, the TiO2 structures are composed of both an…
Tailoring the Structural, Optical, and Photoluminescence Properties of Porous Silicon/TiO2 Nanostructures
2015
The structural, optical, and photoluminescence properties of porous silicon (PSi)/titanium dioxide (TiO2) nanostructures were investigated. PSi structures consisting of macro- and mesoporous layers were fabricated by metal-assisted chemical etching, and then TiO2 was introduced inside the PSi matrix using the atomic layer deposition technique. We performed scanning electron microscopy, transmission electron microscopy (TEM), X-ray diffraction, energy dispersive X-ray spectroscopy, Raman spectroscopy, ellipsometry, and photoluminescence (PL) spectroscopy to characterize the prepared and annealed PSi/TiO2 nanostructures. TEM and Raman analyses revealed that TiO2 had a crystalline anatase stru…
Highly stable defective TiO2-x with tuned exposed facets induced by fluorine: Impact of surface and bulk properties on selective UV/visible alcohol p…
2020
Abstract Titanium dioxide samples were prepared in the presence of different amounts of fluorine via hydrothermal method. It has been found that the presence of fluoride influenced the physico-chemical properties of TiO2 in various ways as polymorphic form stability, surface hydroxylation, generation of hydroxyl radicals under irradiation and formation of Ti3+ centers and oxygen vacancies. The generation rate of OH radicals was investigated by the photoluminescence technique in the presence of terephthalic acid. X-ray diffractometry indicated that fluorine stabilized the anatase TiO2. X-Ray photoelectron spectroscopy (XPS) revealed the presence of fluorine on the surface and the shift of th…
Photocatalytic thin films of TiO2 formed by a sol-gel process using titanium tetraisopropoxide as the precursor
2008
Abstract Thin TiO 2 films were prepared with the dip-coating technique by using sols deriving from titanium tetraisopropoxide. TiO 2 films were formed on glass substrates previously covered by a SiO 2 layer obtained from a tetraethylortosilicate sol. The films, after a thermal treatment at 673 K, mainly consisted of TiO 2 anatase. The samples were characterised by X-ray diffraction, UV–Vis spectroscopy, scanning electron microscopy and atomic force microscopy. The photoactivity of the various films was tested by using as probe reaction the photo-oxidation of 2-propanol in gas-solid regime. The photoreactivity results indicated that the TiO 2 films were efficient for degrading 2-propanol und…
Study of phase composition, photocatalytic activity, and photoluminescence of TiO2 with Eu additive produced by the extraction-pyrolytic method
2021
The Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART2. The work was also partially supported by the LZP grant 2020/2-0074. R. Burve has been supported by the project “Synthesis of nanostructured materials based on titanium dioxide and tin dioxide and investigation of their physicochemical properties” Nr. MP-2019/7, for strengthening scientific personnel capacity 2019/2020 at the Riga Technical University. Authors are grateful to Dr. K. Šmits for the microscopic measurements and SEM images.