Comparative assessment of surface roughness produced by hard machining with mixed ceramic tools including 2D and 3D analysis
2005
Abstract This paper provides a new comprehensive analysis of part surface finish in continuous dry turning of a hardened construction steel when using mixed alumina cutting tools. Consequently, the surface profiles (2D arragement) and surface microstereometries (3D arragement) generated during different hard part turning operations on a 40H low chromium alloy steel (equivalent to AISI 5140 or DIN 41Cr4), heat treated to the hardness of about 60 HRC, were evaluated. As a result, this paper aggregates the multi-parameters characterization of the surface roughness with the machined surface structure obtained at the three selected feed rates and constant cutting speed of 100 m/min. Results show…
Use of pure vanadium and niobium/copper inserts for laser welding of titanium to stainless steel
2020
Abstract Niobium and vanadium have high metallurgical compatibility with titanium and therefore can be used as inserts to avoid the accumulation of brittle intermetallic phases such as Fe2Ti during the fusion welding of titanium alloys with steels. In the present study, the continuous double pass welding of 1 mm thick Ti-6Al-4V alloy and 316 L stainless steel plates through several mm wide pure vanadium or niobium insert was studied. In case of a vanadium insert, a beam offset on the vanadium was found to produce cold crack formation in vanadium/316 L melted zones containing more than 40 wt.% V despite the absence of σ phase. Whereas a centered beam position and offset on the steel side pro…
Optical modeling of nickel-base alloys oxidized in pressurized water reactor
2012
International audience; The knowledge of the aging process involved in the primary water of pressurized water reactor entails investigating a mixed growth mechanism in the corrosion of nickel-base alloys. A mixed growth induces an anionic inner oxide and a cationic diffusion parallel to a dissolution-precipitation process forms the outer zone. The in situ monitoring of the oxidation kinetics requires the modeling of the oxide layer stratification with the full knowledge of the optical constants related to each component. Here, we report the dielectric constants of the alloys 600 and 690 measured by spectroscopic ellipsometry and fitted to a Drude-Lorentz model. A robust optical stratificati…
Laser densification of organic coating: Effects of laser wavelength, operating parameters and substrate properties
2012
International audience; Mechanical bonding and interface behaviour play a key role for any materials deposited on different substrates. Usually, a post-spray heat treatment is required to improve the coating morphology and to enhance mechanical properties of thermal-sprayed polymeric coating. The effects of YAG, CO2 and diode laser radiations on as-sprayed PEEK coating deposited on stainless steel and aluminum substrates were investigated. The results revealed a good coating densification and interface behavior. A correlation between coating and substrate absorption coefficients, their thermophysical properties and laser operating parameters was shown. Besides, the finite element modeling b…
Passivation-Induced Physicochemical Alterations of the Native Surface Oxide Film on 316L Austenitic Stainless Steel
2019
Time of Flight Secondary Ion Mass Spectroscopy, X-Ray Photoelectron Spectroscopy, in situ Photo-Current Spectroscopy and electrochemical analysis were combined to characterize the physicochemical alterations induced by electrochemical passivation of the surface oxide film providing corrosion resistance to 316L stainless steel. The as-prepared surface is covered by a ~2 nm thick, mixed (Cr(III)-Fe(III)) and bi-layered hydroxylated oxide. The inner layer is highly enriched in Cr(III) and the outer layer less so. Molybdenum is concentrated, mostly as Mo(VI), in the outer layer. Nickel is only present at trace level. These inner and outer layers have band gap values of 3.0 and 2.6-2.7 eV, respe…
Repassivation of the damage generated by cavitation on UNS N08031 in a LiBr solution by means of electrochemical techniques and Confocal Laser Scanni…
2010
Abstract The objective of this work is to study the influence of cavitation on the corrosion behaviour of Alloy 31, a highly-alloyed austenitic stainless steel (UNS N08031), in a LiBr heavy brine solution (992 g/L) at 25 °C. The presence of cavitation shifted the OCP value towards the active direction by 708 mVAg/AgCl, increased anodic current densities and passivation current density, ip, and reduced the pitting potential, Ep. Repassivation behaviour of Alloy 31 has been investigated by using potentiostatic tests at different potentials. The current density transient obtained after interrupting cavitation was used to obtain the repassivation index, n, provided by the slope of the log i(t) …
Study of Passive Films Formed on AISI 316L Stainless Steel in Non-Polluted and Underwater-Volcano-Polluted Seawater
2014
This work studies the semiconducting behavior of passive films formed on AISI 316L (UNS S31603) in two different sea-water solutions, non-polluted and polluted, collected from the volcano of El Hierro Island. Polarization measurements, potentiostatic passivation tests, electrochemical impedance spectroscopy, and capacitance measurements were performed. Results show that the polluted seawater worsens passivation kinetics. Additionally, passive films formed on AISI 316L stainless steel in polluted seawater have been found to be less protective than those formed in non-polluted seawater, showing a more defective structure, owing to the acidity of the polluted medium.
Passive Behavior and Passivity Breakdown of AISI 304 in LiBr Solutions through Scanning Electrochemical Microscopy
2014
The passive behavior and passivity breakdown of AISI 304 stainless steel in LiBr solutions has been investigated by means of scanning electrochemical microscopy (SECM). The sample generation - tip collection (SG-TC) mode was used to operate the SECM and the tip potential was biased to detect the electroactive species. The evolution of the current at the ultramicroelectrode tip with the applied potential within the passive range was followed at different LiBr concentrations. Results show that the absolute value of the current at the tip increases with the applied potential. Additionally, SECM was also used to detect stable pits formed on the stainless steel surface in a 0.2 M LiBr solution. …
Inhibition of Cor-Ten steel corrosion by “green” extracts of Brassica campestris
2018
Abstract Extract of Brassica campestris was tested as potential corrosion inhibitor for Cor-Ten steel in NaCl and acidic solutions, simulating a marine and an urban-industrial environment, respectively. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) were performed both in absence and in presence of the extract at room temperature. The surface chemical analysis was investigated by X-ray Photoemission Spectroscopy (XPS), before and after corrosion. Electrochemical results demonstrated that a very small concentration of Brassica campestris extracts can inhibit Cor-Ten corrosion in NaCl solution (inhibition efficiency of 80–84%) better than in acidic solutions. Su…
Simplified Model for Compressive Behavior of Concrete Columns Strengthened by Steel Angles and Strips
2010
This paper presents an analytical model to determine the compressive response of concrete members, having a square transverse cross section and reinforced with steel angles at the corners and steel strips connecting the steel angles. The model evaluates the effects of transverse strips and steel angles on confinement pressures, including strength and buckling phenomena. Compressive response was evaluated in cases of directly and indirectly loaded elements. The data produced correlate well with available experimental data.