Elaboration and characterization of barium silicate thin films.
International audience; Room temperature depositions of barium on a thermal silicon oxide layer were performed in ultra high vacuum (UHV). In-situ X-ray photoelectron spectroscopy (XPS) analyses were carried out as well after exposure to air as after subsequent annealings. These analyses were ex-situ completed by secondary ion mass spectrometry (SIMS) profiles and transmission electron microscopy (TEM) cross-sectional images. The results showed that after air exposure, the barium went carbonated. Annealing at sufficient temperature permitted to decompose the carbonate to benefit of a barium silicate. The silicate layer was formed by interdiffusion of barium with the initial SiO2 layer.
Photoemission study of the reactivity of barium towards SiOx thermal films
Abstract Barium was deposited at room temperature on a thermal silicon oxide layer and the interfacial reaction was monitored by synchrotron induced photoemission (both core level and valence band). The first step of the growth consists of an interfacial reaction which leads to the formation of an interfacial silicate layer. The next step consists in formation of barium oxide while metallic barium occurs subsequently. The deposit can be also homogenized by annealing above 575 K. This results in the formation of several layers of silicate by consumption of silicon oxide. In the case of fractional coverage, subsequent annealing at 975 K induces the decomposition of barium silicate. However, s…