Radiation induced defects in SiO 2

subject

description

The main luminescent centers in SiO 2 films are the red luminescence R (650 v nm; 1.85 v eV) of the non-bridging oxygen hole center (NBOHC) and the twofold-coordinated (divalent) silicon with a blue B (460 v nm; 2.7 v eV) and a UV band (285 v nm; 4.4 v eV). Especially the latter ones are produced under irradiation, but from existing precursors assumed as silicon related oxygen deficient centers (SiODC). Therefore, in order to prove these models we compare a direct oxygen implantation with a direct silicon implantation into SiO 2 layers. The main result is: implanting oxygen increases the red band R but does not affect the blue band B. Silicon surplus increases the amplitude of the blue (B) luminescence, but reduces the amplitude of the red (R) one. Studying the cathodoluminescence dose dependence of these blue and red bands we have established defect transformation kinetics in SiO 2 including six main defects and precursors as well as the mobile oxygen as the main transmitter between precursors and the ra...