Preparation characterization and photocatalytic activity of polycrystalline ZnO/TiO2 systems. 2. Surface, bulk characterization, and 4-nitrophenol ph…
2001
Electron spin resonance spectroscopy (ESR), Fourier transform infrared spectroscopy (FTIR), and monitoring of pyridine (py) and boric acid trimethyl ester (BATE) adsorption for determining surface acidity and basicity, respectively, were used to carry out further characterization of mixed ZnO/TiO2 polycrystalline solids prepared by different methods. Moreover, the powders were tested in a batch photoreactor for a probe reaction, i.e., 4-nitrophenol photodegradation in aqueous medium. ESR results indicated the presence of signals attributable to Zn+ species in ZnO/TiO2 (anatase) solids, while in ZnO/TiO2 (rutile) samples the presence of zinc induced only the formation of signals probably due…
Preparation characterization and photocatalytic activity of polycrystalline ZnO/TiO2 systems. 1. Surface and bulk characterization
2001
Polycrystalline ZnO/TiO2 solids have been prepared with four different methods using home prepared TiO2 (anatase) or TiO2 (rutile) as supports and Zn(NO3)2·6H2O or Zn(CH3COO)2·2H2O as precursors for ZnO. The bulk and surface properties of the samples were investigated by means of TG-DTA, XRD, TEM, SEM-EDAX, XPS, BET surface area determination, and porosity measurements. XRD and TEM results indicate that no significant defect structures exist in any of the samples. The ZnO crystallinity and its enrichment on the surface of TiO2 particles were dependent on the preparation method. The surface areas generally decrease by increasing the amount of ZnO except when ZnO from Zn(CH3COO)2·2H2O was sup…
Preparation and photoactivity of nanostructured anatase, rutile and brookite TiO2 thin films
2006
Photoactive films consisting of pure anatase, brookite or rutile TiO2 were prepared by dip coating from water dispersions obtained by using TiCl4 as the precursor under similar mild experimental conditions
Polyacrylonitrile block copolymers for the preparation of a thin carbon coating around TiO2 nanorods for advanced lithium-ion batteries.
2013
Herein, a new method for the realization of a thin and homogenous carbonaceous particle coating, made by carbonizing RAFT polymerization derived block copolymers anchored on anatase TiO2 nanorods, is presented. These block copolymers consist of a short anchor block (based on dopamine) and a long, easily graphitizable block of polyacrylonitrile. The grafting of such block copolymers to TiO2 nanorods creates a polymer shell, which can be visualized by atomic force microscopy (AFM). Thermal treatment at 700 °C converts the polyacrylonitrile block to partially graphitic structures (as determined by Raman spectroscopy), establishing a thin carbon coating (as determined by transmission electron m…
Thermal effects on the growth by metal organic chemical vapour deposition of TiO2 thin films on (100) GaAs substrates
2002
Abstract TiO 2 thin films were deposited on (100) GaAs substrates by LP-MOCVD with deposition temperatures ( T d ) ranking from 450 to 750 °C. The structure of these layers was studied by X-ray diffraction (XRD) and Raman spectroscopy. The growth of the TiO 2 anatase phase was observed for T d T d >600 °C. Finally, X-ray photoelectron spectrometry (XPS) and secondary ion mass spectroscopy (SIMS) experiments showed the presence of small quantities of Ga and As through the whole film thickness, slightly increasing at the surface of the layers. This result was related to the SEM observations and explained by considering the growth conditions.
Investigation of TiO<sub>2</sub> Ceramic Surface Conductivity Using Conductive Atomic Force Microscopy
2012
Dense TiO2 (rutile) ceramic samples were prepared by sintering compacts of titanium dioxide anatase powder at 1500 °C for 5h. Sintered samples were polished and annealed in vacuum at 1000 °C for 1h. Structural properties of the samples were studied by X-ray diffraction, polarized light and scanning electron microscopy. The surface topography and local electrical conductivity of the samples were investigated by atomic force microscopy technique under atmospheric conditions. Enhanced electrical conductivity was observed at grain boundaries while the polished, vacuum annealed grains surface showed non-homogeneous conductivity.
Investigation on sol–gel synthesized Ag-doped TiO2 cermet thin films
2005
Abstract Undoped TiO 2 and Ag–TiO 2 (up to 23 at.% Ag) cermet thin films and polycrystalline powders have been prepared by sol–gel process. Their structure, composition, surface morphology and optical properties have been investigated by X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and ultraviolet–visible spectroscopy (UV–VIS spectroscopy). It has been observed that while Ag does not form a solid solution with TiO 2 , it promotes the anatase to rutile phase transformation. The transformation temperature decreases from 827 °C for undoped TiO 2 to about 650 °C fo…
TiO2 anatase films obtained by direct liquid injection atomic layer deposition at low temperature
2014
International audience; TiO2 thin films were grown by direct liquid injection atomic layer deposition (DLI-ALD) with infrared rapid thermal heating using titanium tetraisopropoxide and water as precursors. This titanium tetraisopropoxide/water process exhibited a growth rate of 0.018 nm/cycle in a self-limited ALD growth mode at 280 degrees C. Scanning electron microscopy and atomic force microscopy analyses have shown a smooth surface with a low roughness. XPS results demonstrated that the films were pure and close to the TiO2 stoichiometric composition in depth. Raman spectroscopy revealed that the films were crystallized to the anatase structure in the as-deposited state at low temperatu…
Study of the structural changes induced by air oxidation in Ti–Si–N hard coatings.
2008
International audience; 3-μm thick Ti–Si–N coatings were deposited on polished X38CrMoV5 substrates by sputtering a composite Ti–Si target in Ar–N2 reactive mixture. Oxidation tests were performed in air at 700 °C during 2 h. Whatever the silicon content in the range 0–4 at.%, no silicon containing compound was detected by XRD before air oxidation and only the TiN phase was evidenced. The mean grain size estimated from the full width at half maximum of the TiN (111) diffraction peak was close to 10 nm. As commonly reported for Ti–Si–N films, the hardness showed a maximum at 51 GPa versus the Si content. After oxidation of the TiN film, XRD and micro-Raman analyses revealed the occurrence of…
Removal of Surface Oxygen Vacancies Increases Conductance Through TiO(2) Thin Films for Perovskite Solar Cells
2019
[Image: see text] We report that UV–ozone treatment of TiO(2) anatase thin films is an efficient method to increase the conductance through the film by more than 2 orders of magnitude. The increase in conductance is quantified via conductive scanning force microscopy on freshly annealed and UV–ozone-treated TiO(2) anatase thin films on fluorine-doped tin oxide substrates. The increased conductance of TiO(2) anatase thin films results in a 2% increase of the average power conversion efficiency (PCE) of methylammonium lead iodide-based perovskite solar cells. PCE values up to 19.5% for mesoporous solar cells are realized. The additional UV–ozone treatment results in a reduced number of oxygen…