Amorphous Silicon Nanotubes via Galvanic Displacement Deposition
2013
Amorphous silicon nanotubes were grown in a single step into a polycarbonate membrane by a galvanic displacement reaction conducted in aqueous solution. In order to optimize the process, a specifically designed galvanic cell was used. SEM images, after polycarbonate dissolution, showed interconnected nanotube bundles with an average length of 18 μm and wall thickness of 38 nm.The deposited silicon was revealed by EDS analysis, whilst X-ray diffraction and Raman spectroscopy showed that nanotubes have an amorphous structure. Silicon nanotubes were also characterized by photo-electrochemical measurements that showed n-type conductivity and optical gap of ~1.6 eV. Keywords: Silicon nanotubes, …
Influence of the electro-optical properties of an a-Si:H single layer on the performances of a pin solar cell
2012
We analyze the results of an extensive characterization study involving electrical and optical measurements carried out on hydrogenated amorphous silicon (α-Si:H) thin film materials fabricated under a wide range of deposition conditions. By adjusting the synthesis parameters, we evidenced how conductivity, activation energy, electrical transport and optical absorption of an α-Si:H layer can be modified and optimized. We analyzed the activation energy and the pre-exponential factor of the dark conductivity by varying the dopant-to-silane gas flow ratio. Optical measurements allowed to extract the absorption spectra and the optical bandgap. Additionally, we report on the temperature dependen…
Effects of power resistance training program with elastic bands on body composition, muscle strength and physical function in older women
2020
The aim of this study was to investigate the effects of a power-strength resistance program with elastic bands on body composition, physical function, and muscle strength in older women. For such purpose, a randomized controlled trial with a pre-post-intervention design was conducted. Thus, 58 healthy, physically independent, sedentary women, aged 65-85 years, were randomly allocated to the intervention (n = 28) or control group (n = 30). Measurements of body composition (total mass, total fat mass, total skeletal-muscle mass, and body fat percentage), isokinetic muscle strength of knee flexors and extensors (at 60º/second and 180º/second), and physical performance (flexibility, agility/dyn…
Amorphous TiO2 in LP-OMCVD TiNxOy thin films revealed by XPS
2001
Abstract TiN(O)–TiO 2 thin films were prepared on Si(1 0 0) by the low pressure organo metallic chemical vapor deposition (LP-OMCVD) method, using ammonia and titanium isopropoxide as precursors. In order to complete previous characterizations, an Ar + bombardment/XPS coupled study was carried out. This method is based on the fact that the behavior of a compound towards an ion bombardment is a function of its composition. In particular, Ar + bombardment of TiO 2 (whatever its form) leads to a preferential sputtering of oxygen atoms with subsequent reduction of titanium and formation of Ti 3+ and Ti 2+ easily detectable by XPS from a significant broadening of the Ti 2p lines. In the opposite…
Structure and properties of GaNxOy films grown by nitridation of GaAs (100) substrates
2004
GaAs (100) substrates have been heat-treated in a metal-organic chemical vapor deposition reactor under flows of NH 3 and an oxygen organo-metallic precursor at temperatures between 650°C and 750°C. Yellowish films formed at the surface of all the samples. Gallium, nitrogen and oxygen were detected by EDX analysis of the films. The oxygen content was estimated in the range of at 5-10 at% depending on the heat-treatment temperature. X-ray diffraction and HRTEM results indicate that the structure of the films corresponds to the hexagonal wurtzite phase of GaN with an expanded unit cell. Raman spectra show hands corresponding to the Raman active GaN modes as well as disorder-activated broad ba…
Reactive direct current magnetron sputtered TiO2 thin films with amorphous to crystalline structures.
2008
International audience; TiO2 thin films were deposited on soda–lime glass substrates by reactive direct current magnetron sputtering in a mixture of pure argon and oxygen. The influence of both the deposition time, td, and the post-annealing treatments on the films morphology, composition and structure was analyzed by scanning electron microscopy, ellipsometry, X-ray photoelectrons spectroscopy, X-ray diffraction (XRD) and Raman spectroscopy. Amorphous TiO2 was obtained for the shortest deposition time, td=15 min. Increasing td up to 30 min, poorly crystallized anatase and rutile phases were formed together with amorphous TiO2, as was revealed by complementary XRD patterns and Raman spectra…
Nanostructured Pt–TiO2 composite thin films obtained by direct liquid injection metal organic chemical vapor deposition: Control of chemical state by…
2015
Abstract Nanostructured Pt–TiO 2 composite thin films were synthesized by direct liquid injection metal organic chemical vapor deposition process, using trimethyl(methylcyclopentadienyl)platinum and titanium isopropoxide as precursors. Surface and cross-sectional morphologies obtained by scanning electron microscopy and transmission electron microscopy evidenced the uniform distribution of platinum nanoparticles in the TiO 2 matrix. At higher Pt content, the X-ray diffraction analysis showed that the face-centered cubic phase of platinum appeared together with an anatase TiO 2 structure. In addition, as far as the platinum chemical state is concerned, the co-deposition of TiO 2 and Pt allow…
Thermal effects on the growth by metal organic chemical vapour deposition of TiO2 thin films on (100) GaAs substrates
2002
Abstract TiO 2 thin films were deposited on (100) GaAs substrates by LP-MOCVD with deposition temperatures ( T d ) ranking from 450 to 750 °C. The structure of these layers was studied by X-ray diffraction (XRD) and Raman spectroscopy. The growth of the TiO 2 anatase phase was observed for T d T d >600 °C. Finally, X-ray photoelectron spectrometry (XPS) and secondary ion mass spectroscopy (SIMS) experiments showed the presence of small quantities of Ga and As through the whole film thickness, slightly increasing at the surface of the layers. This result was related to the SEM observations and explained by considering the growth conditions.
TiO2 anatase films obtained by direct liquid injection atomic layer deposition at low temperature
2014
International audience; TiO2 thin films were grown by direct liquid injection atomic layer deposition (DLI-ALD) with infrared rapid thermal heating using titanium tetraisopropoxide and water as precursors. This titanium tetraisopropoxide/water process exhibited a growth rate of 0.018 nm/cycle in a self-limited ALD growth mode at 280 degrees C. Scanning electron microscopy and atomic force microscopy analyses have shown a smooth surface with a low roughness. XPS results demonstrated that the films were pure and close to the TiO2 stoichiometric composition in depth. Raman spectroscopy revealed that the films were crystallized to the anatase structure in the as-deposited state at low temperatu…
Core-shell Zn-doped TiO2-ZnO nanofibers fabricated via a combination of electrospinning and metal-organic chemical vapour deposition
2010
Zn-doped TiO2 nanofibers shelled with ZnO hierarchical nanoarchitectures have been fabricated combining electrospinning of TiO2 (anatase) nanofibers and metal-organic chemical vapor deposition (MOCVD) of ZnO. The proposed hybrid approach has proven suitable for tailoring both the morphology of the ZnO external shell as well as the crystal structure of the Zn-doped TiO2 core. It has been found that the Zn dopant is incorporated in calcined electrospun nanofibers without any evidence of ZnO aggregates. Effects of different Zn doping levels of Zn-doped TiO2 fibers have been scrutinized and morphological, structural, physico-chemical and optical properties evaluated before and after the hierarc…